Block copolymers and uses thereof

1. A styrenic block copolymer having one or more polymer blocks A and one or more polymer blocks B and having a formula selected from: A-B-A, A-B-B-A, (A-B-A) n X, (A-B) n X, or mixtures thereof, wherein

n is from 2 to 30, X is residue of a coupling agent;

the block copolymers containing at least two blocks A connected by at least one block B representing more than 50 wt. % of the styrenic block copolymer;

each one or more A block independently is a polystyrene block having:

a 1,1-diphenylethylene content from about 10 wt. % to about 63 wt. %, relative to the weight of the A block,

a molecular weight from about 5 kg/mol to about 40 kg/mol, and

a weight content relative to the weight of the styrenic block copolymer, of about 10 wt. % to about 40 wt. %;

each one or more B block independently is a poly(1,3-diene-styrene) block derived from 1,3-diene units and styrene units, the poly(1,3-diene-styrene) block comprises an isoprene-rich block, a butadiene-rich block, or combinations of both blocks, wherein

the polymerized 1,3-diene units having pendant 1,2- and/or 3,4-vinyl groups correspond to a wt. % content “V” as relative to the total weight of the polymerized 1,3-diene in the one or more B blocks,

the styrene unit having wt.% content “S” as relative to total weight of the one or more B blocks,

the isoprene-rich block if present comprises more than 90 wt. % of polymerized isoprene units relative to the weight of the polymerized 1,3-diene, with S having a value of 0 to about 40, and (S+V) having a value of about 18 to about 75,

the butadiene-rich block if present comprises more than 90 wt. % of polymerized butadiene units relative to the weight of the polymerized 1,3-diene, with S having a value of 0 to about 40, and (1.2*S+V) having a value about 60 to about 120.

2. The styrenic block copolymer of claim 1 , wherein the block copolymer is hydrogenated, and wherein subsequent to hydrogenation, up to 10 percent of the aromatic double bonds have been hydrogenated, and at least 80 percent of the diene double bonds have been hydrogenated.

3. The styrenic block copolymer of claim 2 , wherein each one or more A block independently has a molecular weight from about 10 kg/mol to 20 kg/mol.

4. The styrenic block copolymer of claim 1 , which exhibits a DMA tangent delta maximum at a temperature between −40° C. and +10° C., at 10 rad/s angular frequency, as measured in accordance with ASTM D4065.

5. The styrenic block copolymer of claim 1 , which exhibits a 10% loss in elastic modulus relative to an extrapolated rubbery plateau modulus at a temperature greater than 110° C.

6. The styrenic block copolymer of claim 1 , wherein each one or more A block independently has

a 1,1-diphenylethylene content from about 15 to about 60 wt. %, relative to the weight of the A block;

a molecular weight from about 10 kg/mol to about 25 kg/mol; and

a weight content relative to the weight of the styrenic block copolymer, of about 13 wt. % to about 25 wt. %; and

each one or more B block independently comprises

an isoprene-rich block if present comprising more than 90 wt. % of polymerized isoprene units relative to the weight of the polymerized 1,3-diene, with S having a value of 0 to about 25, and (S+V) having a value of about 25 to about 65;

a butadiene-rich block if present comprising more than 90 wt. % of polymerized butadiene units relative to the weight of the polymerized 1,3-diene, with S having a value of 10 to about 30, and (1.2*S+V) having a value of about 60 to about 100.

7. The styrenic block copolymer of claim 1 ,

wherein each one or more A block independently has a 1,1-diphenylethylene content from about 20 wt. % to about 50 wt. %, relative to the weight of the A block; and

n is from about 2 to about 10;

wherein the styrenic block copolymers comprising at least two A blocks connected by at least one B block represent more than 80 wt. % of the styrenic block copolymer.

8. The styrenic block copolymer of claim 1 , further comprising one or more C blocks, wherein the C block is between the A block and the B block, and is a poly(1,3-diene) block substantially free of styrene units.

9. The styrenic block copolymer of claim 8 , having a formula A-C-B-C-A or (A-C-B) n X; wherein n is from 2 to 30, and X is residue of a coupling agent.

10. The styrenic block copolymer of claim 8 , wherein the B and C blocks together comprise

a wt. % styrene content “S 1 ” relative to the weight of the one or more B and C blocks; and a wt. % 1,3-diene content having pendant 1,2- and/or 3.4-vinyl groups “V 1 ”, relative to the weight of the polymerized 1,3-diene in the one or more B and C blocks;

wherein the one or more B and C blocks together comprise

an isoprene-rich block if present comprising more than 90 wt. % of polymerized isoprene units relative to the weight of the polymerized 1,3-diene, with S 1 having a value of 0 to about 40, and (S 1 +V 1 ) having a value of about 18 to about 75;

a butadiene-rich block if present comprising more than 90 wt. % of polymerized butadiene units relative to the weight of the polymerized 1,3-diene, with S 1 having a value of 0 to about 40, and (1.2*S 1 +V 1 ) having a value of about 60 to about 120.

11. The styrenic block copolymer of claim 1 , wherein each one or more A block independently has a molecular weight from about 13 kg/mol to 26 kg/mol.

12. A thermoplastic elastomer blend comprising:

99%-1% of the styrenic block copolymer of claim 1 , and

1%-99% of one or more components selected from (a) at least one plasticizer, (b) at least one resin, (c) at least one additive, (d) at least one filler, and (e) at least one plastic material.

13. An adhesive composition comprising the styrenic block copolymer of claim 1 .

14. An adhesive composition comprising the styrenic block copolymer of claim 2 .

15. An adhesive composition comprising the styrenic block copolymer of claim 8 .

16. A sound or vibration damping composition comprising the styrenic block copolymer of claim 1 .

17. A styrenic block copolymer having one or more polymer blocks A and one or more polymer blocks B and having a formula selected from: A-B-A, A-B-B-A, (A-B-A) n X, (A- B) n X, or mixtures thereof, wherein

n is from 2 to 30, X is residue of a coupling agent;

the block copolymers containing at least two blocks A connected by at least one block B representing more than 50 wt. % of the styrenic block copolymer;

each one or more A block independently is a polystyrene block having:

a 1,1-diphenylethylene content from about 10 wt. % to about 63 wt. %, relative to the weight of the A block,

a molecular weight from about 5 kg/mol to about 40 kg/mol, and

a weight content relative to the weight of the styrenic block copolymer, of about 13 wt. % to about 25 wt. %;

each one or more B block independently is a poly(1,3-diene-styrene) block derived from 1,3-diene units and styrene units, the poly(1,3-diene-styrene) block comprises an isoprene-rich block, a butadiene-rich block, or combinations of both blocks, wherein

the polymerized 1,3-diene units having pendant 1,2- and/or 3,4-vinyl groups correspond to a wt.% content “V” as relative to the total weight of the polymerized 1,3- diene in the one or more B blocks,

the styrene unit having wt.% content “S” as relative to total weight of the one or more B blocks,

the isoprene-rich block if present comprises more than 90 wt. % of polymerized isoprene units relative to the weight of the polymerized 1,3-diene, with S having a value of 0 to about 25, and (S+V) having a value of about 25 to about 65, and

the butadiene-rich block if present comprises more than 90 wt. % of polymerized butadiene units relative to the weight of the polymerized 1,3-diene, with S having a value of 10 to about 30, and (1.2*S+V) having a value of about 60 to about 100;

wherein the styrenic block copolymer exhibits a DMA tangent delta maximum at a temperature between -40° C. and +10° C., at 10 rad/s angular frequency, as measured in accordance with ASTM D4065.