Clear sprayable sealant for aircraft parts and assemblies
Applicant discloses a two part polymer mix for use in the aircraft industry that is applied with pneumatic mix and spray gun. The two part cartridge is used in the mix and spray gun so the mix is applied immediately upon mixing, but the two components are kept separated unless the gun is applying the mix. The mix cures to form a clear sealant that allows for inspection of cracks and corrosion beneath the sealant. It cures quickly so that the coated part may be further processed, for example in the assembly line during aircraft build.
1. A method for coating an aircraft part with a sealant, comprising the steps of: providing a pneumatic, mix and spray gun with a mixing straw and two chambers,
a first chamber having a first mix component with a viscosity of 1000 to 1800 cps and a separate second chamber having a second mix component with a viscosity of 250 to 500 cps, the mix and spray gun configured to mix and emit a spray of atomized, uncured mix from the tip of a mixing nozzle;
first directly applying to a first section of a first workpiece at ambient temperature a first layer of uncured mix; allowing the uncured mix to cure at ambient temperature to form a clear sealant coating, the sealant coating being one of a polyurea, a polyurethane or hybrid coating; and wherein the allowing step takes about 100 minutes or less at 77° F. for the mix to reach dry hard.
2. The method of claim 1 , wherein the allowing step takes about 30 minutes or less at 77° F.
3. The method of claim 1 , wherein the first applying step is airless or air assisted.
4. The method of claim 1 , further including a second applying to the first layer a second layer of uncured mix.
5. The method of claim 4 , wherein the first layer is 10 mil or less in thickness.
6. The method of claim 1 , wherein the mix, prior to gelling, is 4000 cps or less.
7. The method of claim 4 , wherein the mix prior to gelling is 4000 cps or less.
8. The method of claim 4 , wherein the first layer is 10 mil or less in thickness, and wherein the mix prior to gelling is 4000 cps or less.