This invention is in the field of surface modification. In particular, the invention relates to the surface modification of microfluidic devices to alter surface hydrophobicity characteristics.
1. A method of functionalizing the surface of a microfluidic channel comprising the steps of:
a) providing;
i) an enclosed microfluidic channel comprising an unmodified surface;
ii) a bifunctional crosslinker selected from the group consisting of ANB-NOS, Sulfo-SAND, SANPAH and Sulfo-SANPAH;
iii) surface hydrophobicity modifying molecules selected from the group consisting of PEG, TRIS, poly vinyl alcohol, and PLA;
b) exposing at least a portion of said unmodified surface to said bifunctional crosslinker;
c) activating said crosslinker under first conditions to create a crosslinked; and
d) exposing said crosslinked surface to said surface hydrophobicity modifying molecules under second conditions to create a functionalized surface.
2. The method of claim 1 , wherein said enclosed microfluidic channel is a portion of a microfluidic device.
3. The method of claim 1 , wherein said enclosed microfluidic channel is.
4. The method of claim 1 , wherein said enclosed microfluidic channel further comprises a bubble.
5. The method of claim 4 , further comprising the step of clearing said bubble from said enclosed microfluidic channel.
6. The method of claim 1 , wherein said activating of step c) is done without added heat.
7. The method of claim 1 , wherein said PEG is an amine-terminated PEG.
8. The method of claim 1 , further comprising step e) seeding said enclosed microfluidic channel with cells.
9. The method of claim 8 , wherein said functionalized surface prevents cell attachment.
10. The method of claim 8 , wherein said functionalized surface promotes cell attachment.
11. The method of claim 8 , wherein said unmodified surface of step a) comprises naturally occurring moieties selected from the group consisting of double bonds, C—H sites, N—H sites, and nucleophiles.
12. The method of claim 11 , wherein said nucleophiles are selected from the group consisting of primary amines, alcohols, azide, amines, and amides.
13. The method of claim 1 , further comprising the step of masking at least a region of said unmodified surface of said channel so as to create a masked portion and an unmasked portion.
14. The method of claim 1 , wherein said unmodified surface comprises PDMS.
15. The method of claim 14 , wherein said first conditions comprise exposing said crosslinker to light.
16. The method of claim 15 , wherein said exposure to light comprises rastering or pattern projection.