Process for bonding a textile material to an elastomer

1. A process for adhering a textile material to an elastomer, the process comprising the steps of:

a) pretreating the textile material with at least one polyester of an α-β-unsaturated carboxylic acid;

b) contacting the pretreated textile material with an unvulcanized elastomer; and

c) vulcanizing the product obtained from the step of contacting the pretreated textile material with an unvulcanized elastomer;

wherein the textile material is not treated with resorcinol-formaldehyde latex in the process for adhering a textile material to an elastomer.

2. The process as claimed in claim 1 , wherein the textile material is selected from the group consisting of fibers, threads, sheet textiles and combinations thereof.

3. The process as claimed in claim 2 , wherein the sheet textiles are selected from the group consisting of woven fabrics, knitted fabrics, nonwovens and combinations thereof.

4. The process as claimed in claim 1 , wherein the textile material comprises a material selected from the group consisting of polyester, polyamide, aramid, polyurethane, glass, carbon, viscose and combinations thereof.

5. The process as claimed in claim 1 , wherein the textile material is selected from the group consisting of woven polyester fabric, woven polyamide fabric, polyester thread, aramid thread, aramid fibers, glass fibers, carbon fibers, viscose fibers and combinations thereof.

6. The process as claimed in claim 1 , wherein the at least one polyester of an α-β-unsaturated carboxylic acid is selected from the group consisting of trimethylolpropane trimethacrylate, trimethylolpropane triacrylate and combinations thereof.

7. The process as claimed in claim 1 , wherein the unvulcanized elastomer is a rubber component selected from the group consisting of an ethylene-propylene copolymer (EPM), an ethylene-propylene-diene copolymer (EPDM), a hydrogenated nitrile rubber (HNBR), a chloroprene rubber (CR), a fluoro rubber (FKM), a natural rubber (NR), a styrene-butadiene rubber (SBR), a butadiene rubber (BR) and combinations thereof.

8. The process as claimed in claim 1 , wherein the textile material that has been pretreated with the at least one polyester of an α-β-unsaturated carboxylic acid is broken down into smaller parts or fragments prior to being contacted with the unvulcanized elastomer and is subsequently contacted with the unvulcanized elastomer by being mixed into the unvulcanized elastomer.

9. The process as claimed in claim 8 , wherein the textile material is short aramid fiber, the at least one polyester of an α-β-unsaturated carboxylic acid is trimethylolpropane trimethacrylate and the elastomer is ethylene-propylene-diene copolymer (EPDM) or a hydrogenated nitrile rubber (HNBR).

10. The process as claimed in claim 1 , wherein an elastomer article is obtainable by the process.

11. The process as claimed in claim 10 , wherein the elastomer article is a tape, strap, belt, hose, air spring bellows, expansion joint or a multilayer fabric web.

12. The process as claimed in claim 10 , wherein the elastomer article is a drive belt, wherein the elastomer forms a main body comprising a top ply as belt backing and a substructure having a power transmission zone, wherein the top ply and/or the power transmission zone has/have been provided with the textile material.

13. The process as claimed in claim 12 , wherein the drive belt is designed as a flat belt, V-belt, a V-ribbed belt, a toothed belt, a clutch belt or an elevator belt.

14. The process as claimed in claim 12 , wherein the textile material is short aramid fiber, wherein the at least one polyester of an α-β-unsaturated carboxylic acid is trimethylolpropane trimethacrylate, and wherein the unvulcanized elastomer is ethylene-propylene-diene copolymer (EPDM).

15. The process as claimed in claim 12 , wherein the textile material is short aramid fiber, wherein the at least one polyester of an α-β-unsaturated carboxylic acid is trimethylolpropane trimethacrylate, and wherein the unvulcanized elastomer is hydrogenated nitrile rubber (HNBR).

16. The process as claimed in claim 12 , wherein the textile material is short aramid fiber, the α-β-unsaturated carboxylic acid is trimethylolpropane trimethacrylate and the unvulcanized elastomer is peroxidically crosslinked HNBR.

17. The process as claimed in claim 12 , wherein the textile material is short aramid fiber having a length in the range of from 4 cm to 8 cm.

18. The process as claimed in claim 12 , wherein the textile material that has been pretreated with the at least one polyester of an α-β-unsaturated carboxylic acid is broken down into smaller parts or fragments prior to being contacted with the unvulcanized elastomer and is subsequently contacted with the unvulcanized elastomer by being mixed into the unvulcanized elastomer.