Carbon fiber and method of manufacturing same
By sequentially performing: a step (I) of dissolving fullerene C 60 in a polyalkylene glycol to prepare a fullerene solution; a step (II) of immersing a material carbon fiber in the fullerene solution; and a step (III) of extracting the carbon fiber from the fullerene solution, washing the extracted carbon fiber with water, and drying the carbon fiber washed with water, a carbon fiber on which fullerene C 60 adsorbs is obtained.
1. A method of manufacturing a carbon fiber on which fullerene C 60 adsorbs, the method comprising sequentially performing:
dissolving fullerene C 60 in a polyalkylene glycol to prepare a fullerene solution;
immersing a material carbon fiber in the fullerene solution; and
extracting the carbon fiber from the fullerene solution, washing the extracted carbon fiber with water, and drying the carbon fiber washed with water.
2. The method of manufacturing the carbon fiber according to claim 1 , wherein a concentration of the fullerene C 60 in the solution is 1 ppm by mass to 1000 ppm by mass.
3. The method of manufacturing the carbon fiber according to claim 1 , wherein the polyalkylene glycol is at least one kind selected from diethylene glycol, triethylene glycol, polyethylene glycol, dipropylene glycol, tripropylene glycol, and polypropylene glycol.
4. The method of manufacturing the carbon fiber according to claim 1 , wherein the material carbon fiber is a polyacrylonitrile-based carbon fiber.
5. The method of manufacturing the carbon fiber according to claim 1 , wherein a time of immersing the material carbon fiber is 5 seconds to 24 hours.
6. The method of manufacturing the carbon fiber according to claim 1 , wherein a temperature of the solution during immersion is 10° C. to 100° C.