Optical laminate
An optical laminate is provided where stable durability is secured even at a high temperature, particularly an ultrahigh temperature of about 100° C. or higher, a foaming phenomenon or the like in a pressure-sensitive adhesive layer is also suppressed or prevented, other physical properties required for the optical laminate are also excellent, and even in the case of being disposed adjacent to the electrode, corrosion of the relevant electrode or the like is not induced.
1. An optical laminate comprising:
an optical element including an optical film having a water vapor transmission rate of 100 g/(m 2 ·day) or less as measured at a temperature of 37° C. and 88.5% relative humidity for 24 hours; and
a pressure-sensitive adhesive layer formed on a side of the optical element,
wherein the pressure-sensitive adhesive layer comprises a pressure-sensitive adhesive polymer having an alkyl (meth)acrylate unit having an alkyl group with 4 or more carbon atoms, an alkyl (meth)acrylate unit having an alkyl group with 3 or less carbon atoms, an aromatic group-containing monomer unit and a polar functional group-containing monomer unit that has a carboxyl group,
wherein the polar functional group-containing monomer unit is present in an amount of 1.5 to 4.5 parts by weight relative to 100 parts by weight of the alkyl (meth)acrylate unit having an alkyl group with 4 or more carbon atoms;
wherein the pressure-sensitive adhesive layer has a ratio of a loss tangent (tan δ) at 100° C. to a loss tangent (tan δ) at 30° C. of 1.7 or less, and
wherein the pressure-sensitive adhesive layer has a gel fraction of 70 wt % or more, according to Equation 1 below:
Gel content= B/A ×100 [Equation 1]
wherein, A is a mass (unit: g) of the pressure-sensitive adhesive layer before immersing the pressure-sensitive adhesive layer in ethyl acetate, and B is a dry mass (unit: g) of an insoluble fraction recovered after immersing the pressure-sensitive adhesive layer in ethyl acetate at room temperature for 24 hours, wherein an amount of the alkyl (meth)acrylate unit having an alkyl group with 4 or more carbon atoms in the pressure-sensitive adhesive polymer is in a range of 50 wt % to 70 wt %, wherein the alkyl (meth)acrylate unit having an alkyl group with 3 or less carbon atoms is included in the pressure-sensitive adhesive polymer in an amount of 30 to 65 parts by weight relative to 100 parts by weight of the alkyl (meth)acrylate unit having an alkyl group with 4 or more carbon atoms.
2. The optical laminate according to claim 1 , wherein the optical film having a water vapor transmission rate of 100 g/(m 2 ·day) or less as measured at a temperature of 37° C. and 88.5% relative humidity for 24 hours is a cycloolefin polymer film, an acrylic film or a polyester film.
3. The optical laminate according to claim 1 , wherein the optical element is a polarizing plate.
4. The optical laminate according to claim 3 , wherein the polarizing plate comprises a polarizer and the optical film formed on a side of the polarizer.
5. The optical laminate according to claim 4 , wherein the polarizer is a polyvinyl alcohol polarizer comprising a potassium component and a zinc component.
6. The optical laminate according to claim 5 , wherein a ratio (K/Zn) of the potassium component (K) and the zinc component (Zn) in the polyvinyl alcohol polarizer is in a range of 0.2 to 6.
7. The optical laminate according to claim 5 , wherein the potassium component is included in an amount of 0.1 to 2 wt % based on a total weight of the polyvinyl alcohol polarizer.
8. The optical laminate according to claim 1 , wherein an amount of the alkyl (meth)acrylate unit having an alkyl group with 4 or more carbon atoms in the pressure-sensitive adhesive polymer is in a range of 50 wt % to 65 wt %.
9. The optical laminate according to claim 1 , wherein the alkyl (meth)acrylate unit having an alkyl group with 3 or less carbon atoms is a methyl acrylate unit.
10. The optical laminate according to claim 1 , wherein the alkyl (meth)acrylate unit having an alkyl group with 3 or less carbon atoms is included in the pressure-sensitive adhesive polymer in an amount of 30 to 58 parts by weight relative to 100 parts by weight of the alkyl (meth)acrylate unit having an alkyl group with 4 or more carbon atoms.
11. The optical laminate according to claim 1 , wherein the aromatic group-containing monomer is represented by Formula 1 below:
wherein, R1 represents hydrogen or alkyl, A represents alkylene, n represents an integer in a range of 0 to 3, Q represents a single bond, —O—, —S— or alkylene, and P represents an aromatic ring.
12. The optical laminate according to claim 1 , wherein the aromatic group-containing monomer unit is included in the pressure-sensitive adhesive polymer in an amount of 20 to 45 parts by weight relative to 100 parts by weight of the alkyl (meth)acrylate unit having an alkyl group with 4 or more carbon atoms.
13. The optical laminate according to claim 1 , wherein the polar functional group-containing monomer unit is selected from a group consisting of (meth)acrylic acid, 2-(meth)acryloyloxyacetic acid, 3-(meth)acryloyloxypropyl acid, 4-(meth)acryloyloxybutyric acid, an acrylic acid dimer, itaconic acid, maleic acid and maleic anhydride.
14. The optical laminate according to claim 1 , wherein the polar functional group-containing monomer unit is included in the pressure-sensitive adhesive polymer in an amount of 1.5 to 2 parts by weight relative to 100 parts by weight of the alkyl (meth)acrylate unit having an alkyl group with 4 or more carbon atoms.
15. The optical laminate according to claim 14 , wherein the polar functional group-containing monomer unit is selected from a group consisting of (meth)acrylic acid, 2-(meth)acryloyloxyacetic acid, 3-(meth)acryloyloxypropyl acid, 4-(meth)acryloyloxybutyric acid, an acrylic acid dimer, itaconic acid, maleic acid and maleic anhydride.
16. The optical laminate according to claim 1 , wherein the pressure-sensitive adhesive layer has a room temperature storage elastic modulus of 0.06 MPa or more.
17. The optical laminate according to claim 1 , wherein the pressure-sensitive adhesive layer further comprises a crosslinking agent for crosslinking the pressure-sensitive adhesive polymer.
18. A display device comprising a display panel to which the optical laminate of claim 1 is attached via the pressure-sensitive adhesive layer.
19. The display device according to claim 18 , further comprising an electrode wherein the pressure-sensitive adhesive layer directly contacts the electrode.
20. The optical laminate according to claim 1 , wherein the pressure-sensitive adhesive layer has a room temperature storage elastic modulus from 0.06 MPa to 0.2 MPa.