Positive electrode active material for lithium secondary batteries, positive electrode for lithium secondary batteries, and lithium secondary battery

1. A positive electrode active material for a lithium secondary battery, which is in the form of particles, and comprises a lithium-containing composite metal compound in the form of secondary particles that are aggregates of primary particles capable of being doped and undoped with lithium ions, each of the secondary particles having on its surface a coating layer comprising a metal composite oxide comprising lithium and aluminum, and having a lithium ion conductivity, wherein the positive electrode active material comprises at least nickel and aluminum as non-lithium metals,

wherein a lithium carbonate content is 0.3% by mass or less and a lithium hydroxide content is 0.3% by mass or less, and

wherein the positive electrode active material satisfies all of requirements (1) to (2) below:

(1) [Ave(AR 3 /AR 10 )]/[σ(AR 3 /AR 10 )], which is a reciprocal of coefficient of variation [σ(AR 3 /AR 10 )]/[Ave(AR 3 /AR 10 )], is 6.1 or more, wherein:

AR is a ratio of a detection intensity of aluminum and a detection intensity of nickel (detection intensity of aluminum/detection intensity of nickel), each measured by scanning electron microscopy-energy dispersive X-ray spectroscopy (SEM-EDX) with respect to surfaces of the particles of the positive electrode active material for a lithium secondary battery,

AR 3 is AR when the SEM-EDX is performed at an acceleration voltage of 3 kV,

AR 10 is AR when the SEM-EDX is performed at an acceleration voltage of 10 kV,

[Ave(AR 3 /AR 10 )] is an average of values of a ratio of the AR 3 to the AR 10 [AR 3 /AR 10 ],

[σ(AR 3 /AR 10 )] is a standard deviation of values of a ratio of the AR 3 to the AR 10 [AR 3 /AR 10 ], and

[σ(AR 3 /AR 10 )]/[Ave(AR 3 /AR 10 )] is a coefficient of variation calculated from the average and the standard deviation, and

(2) an average value of AR 3 is 0.025 or more.

2. A positive electrode active material for a lithium secondary battery, which is in the form of particles, and comprises a lithium-containing composite metal compound in the form of secondary particles that are aggregates of primary particles capable of being doped and undoped with lithium ions, each of the secondary particles having on its surface a coating layer comprising a metal composite oxide comprising lithium and zirconium, and having a lithium ion conductivity, wherein the positive electrode active material comprises at least nickel and zirconium as non-lithium metals,

wherein a lithium carbonate content is 0.3% by mass or less and a lithium hydroxide content is 0.3% by mass or less, and

wherein the positive electrode active material satisfies all of requirements (1) to (2) below:

(1) [Ave(ZR 5 /ZR 10 )]/[σ(ZR 5 /ZR 10 )], which is a reciprocal of coefficient of variation [σ(ZR 5 /ZR 10 )]/[Ave(ZR 5 /ZR 10 )], is 1.0 or more, wherein:

ZR is a ratio of a detection intensity of zirconium and a detection intensity of nickel (detection intensity of zirconium/detection intensity of nickel), each measured by scanning electron microscopy-energy dispersive X-ray spectroscopy (SEM-EDX) with respect to surfaces of the particles of the positive electrode active material for a lithium secondary battery,

ZR 5 is ZR when the SEM-EDX is performed at an acceleration voltage of 5 kV,

ZR 10 is ZR when the SEM-EDX is performed at an acceleration voltage of 10 kV,

[Ave(ZR 5 /ZR 10 )] is an average of values of a ratio of the ZR 5 to the ZR 10 [ZR 5 /ZR 10 ],

[σ(ZR 5 /ZR 10 )] is a standard deviation of values of a ratio of the ZR 5 to the ZR 10 [ZR 5 /ZR 10 ], and

[σ(ZR 5 /ZR 10 )]/[Ave(ZR 5 /ZR 10 )] is a coefficient of variation calculated from the average and the standard deviation, and

(2) an average value of ZR 5 is 0.002 or more.

3. A positive electrode active material for a lithium secondary battery, which is in the form of particles, and comprises a lithium-containing composite metal compound in the form of secondary particles that are aggregates of primary particles capable of being doped and undoped with lithium ions, each of the secondary particles having on its surface a coating layer comprising a metal composite oxide comprising lithium and tungsten, and having a lithium ion conductivity, wherein the positive electrode active material comprises at least nickel and tungsten as non-lithium metals,

wherein a lithium carbonate content is 0.3% by mass or less and a lithium hydroxide content is 0.3% by mass or less, and

wherein the positive electrode active material satisfies all of requirements (1) to (2) below:

(1) [Ave(WR 3 /WR 10 )]/[σ(WR 3 /WR 10 )], which is a reciprocal of coefficient of variation [σ(WR 3 /WR 10 )]/[Ave(WR 3 /WR 10 )], is 2.5 or more, wherein:

WR is a ratio of a detection intensity of tungsten and a detection intensity of nickel (detection intensity of tungsten/detection intensity of nickel), each measured by scanning electron microscopy-energy dispersive X-ray spectroscopy (SEM-EDX) with respect to surfaces of the particles of the positive electrode active material for a lithium secondary battery,

WR 3 is WR when the SEM-EDX is performed at an acceleration voltage of 3 kV,

WR 10 is WR when the SEM-EDX is performed at an acceleration voltage of 10 kV,

[Ave(WR 3 /WR 10 )] is an average of values of a ratio of the WR 3 to the WR 10 [WR 3 /WR 10 ],

[σ(WR 3 /WR 10 )] is a standard deviation of values of a ratio of the WR 3 to the WR 10 [WR 3 /WR 10 ], and

[σ(WR 3 /WR 10 )]/[Ave(WR 3 /WR 10 )] is a coefficient of variation calculated from the average and the standard deviation, and

(2) an average value of WR 3 is 0.005 or more.

4. The positive electrode active material according to claim 1 , which has a BET specific surface area of 0.1 m 2 /g or more and 2.0 m 2 /g or less.

5. The positive electrode active material according to claim 1 , which has a water content of 600 ppm or less.

6. The positive electrode active material according to claim 1 , wherein the lithium-containing composite metal compound has an α-NaFeO 2 type crystal structure represented by formula (A) below:

Li[Li x (Ni a Co b Mn c M 1 d ) 1-x ]O 2   (A)

wherein −0.1≤x≤0.2, 0.5≤a<1, 0≤b≤0.3, 0≤c≤0.3, 0≤d≤0.1, a+b+c+d=1, and M 1 is at least one metal selected from the group consisting of Mg, Ca, Sr, Ba, Zn, B, Al, Ga, Ti, Zr, Ge, Fe, Cu, Cr, V, W, Mo, Sc, Y, Nb, La, Ta, Tc, Ru, Rh, Pd, Ag, Cd, In, and Sn.

7. The positive electrode active material according to claim 6 , wherein x in the formula (A) satisfies the following relationship: 0<x≤0.1.

8. A positive electrode for a lithium secondary battery, comprising the positive electrode active material of claim 1 .

9. A lithium secondary battery, comprising the positive electrode of claim 8 .