Embedded conductive wires in polymer artificial muscle actuating devices
An actuating device and a method for manufacturing an actuating device, where the method includes wrapping a conductive wire ( 204 ) around a polymer fiber ( 202 ) at a set tension, and heating the polymer fiber and wire to a temperature that exceeds the glass transition temperature of the polymer fiber for a predetermined amount of time to partially embed the conductive wire into the polymer fiber. The method also includes cooling the polymer fiber and wire to below the glass transition temperature resulting in a wired polymer fiber wherein at least part of the conductive wire is embedded in the polymer fiber.
1. An actuating device comprising:
a polymer fiber; and
a conductive wire,
wherein
the conductive wire is wrapped around the polymer fiber, and
at least part of the conductive wire is embedded into the polymer fiber.
2. The actuating device of claim 1 , wherein at least 5% of the diameter of the conductive wire is embedded into the polymer fiber.
3. The actuating device of claim 1 , wherein the conductive wire comprises one selected from the group of: stainless steel and nichrome alloy.
4. The actuating device of claim 1 , wherein the polymer fiber comprises one selected from the group of: nylon, Polyethylene, Polyvinylidene fluoride, and PolyEtherEtherKetone.
5. The actuating device of claim 1 , wherein the polymer fiber comprises nylon and the conductive wire comprises stainless steel.
6. The actuating device of claim 1 , wherein the conductive wire is uniformly wrapped around the polymer fiber.
7. The actuating device of claim 1 , wherein the conductive wire is non-uniformly wrapped around the polymer fiber based on a desired actuation.
8. The actuating device of claim 1 , wherein a ratio of the diameter of the fiber relative to the diameter of the wire is about 10:1.
9. A method of manufacturing an actuating device, the method comprising:
wrapping a conductive wire around a polymer fiber at a set tension;
heating the polymer and conductive wire to a temperature that exceeds the glass transition temperature of the polymer fiber;
cooling the polymer and conductive wire to below the glass transition temperature resulting in a wired polymer fiber wherein at least part of the conductive wire is embedded in the polymer fiber.
10. The method of claim 9 , wherein the temperature is at least 50° C. below melting temperature of the polymer.
11. The method of claim 9 , wherein the temperature is less or equal to 30° C. below the melting temperature of the polymer.
12. The method of claim 9 , wherein at least 5% of the diameter of the conductive wire is embedded into the polymer fiber.
13. The method of claim 9 , wherein the conductive wire comprises one selected from the group of: stainless steel and nichrome alloy.
14. The method of claim 9 , wherein the polymer fiber comprises one selected from the group of: nylon, Polyethylene, Polyvinylidene fluoride, and PolyEtherEtherKetone.
15. The method of claim 9 , wherein the polymer fiber comprises nylon and the conductive wire comprises stainless steel.
16. The method of claim 9 , wherein the conductive wire is uniformly wrapped around the polymer fiber.
17. The method of claim 9 , wherein the conductive wire is non-uniformly wrapped around the polymer fiber based on a desired actuation.
18. The method of claim 9 , wherein a ratio of the diameter of the fiber relative to the diameter of the wire is about 10:1.
19. The actuating device of claim 1 , wherein the polymer fiber has a diameter of from 50 μm 1 mm.