Cable made from crosslinkable composition without antioxidant and with beneficial methane formation
The invention relates to a cable comprising layer(s), which layer(s), is/are obtained from a polymer composition, wherein the polymer composition comprises a polyethylene and a crosslinking agent, wherein the polymer composition contains a total amount of vinyl groups which is B vinyl groups per 1000 carbon atoms, and B 1 ≤B, wherein B 1 is 0.88, when measured prior to crosslinking according to method ASTM D6248-98; and wherein the crosslinking agent is present in an amount which is Z wt %, prior to crosslinking, based on the total amount (100 wt %) of the polymer composition, and Z≤Z 2 , wherein Z 2 is 0.60, the cable, e.g. being a power cable, and processes for producing the cable; the cable useful in different end applications, such as wire and cable (W&C) applications.
1. A cable comprising layer(s), wherein the layer(s), is/are obtained from a polymer composition, wherein the polymer composition comprises:
a polyethylene and a crosslinking agent,
characterized in that:
the polymer composition contains a total amount of vinyl groups which is B vinyl groups per 1000 carbon atoms, and B 1 ≤B, wherein B 1 is 0.88, when measured prior to crosslinking according to method ASTM D6248-98; and
the crosslinking agent is present in an amount which is Z wt %, prior to crosslinking, based on the total amount (100 wt %) of the polymer composition, and Z≤−Z 2 , wherein Z 2 is 0.60;
wherein said layer(s) is/are crosslinked, and the decomposition of the crosslinking agent during the crosslinking results in a content of less than 200 ppm of methane, and said crosslinked layer(s) has/have a hot set elongation, with a load of 20 N/cm 2 , which is less than 175%.
2. The cable of claim 1 , wherein the polyethylene is unsaturated.
3. The cable of claim 1 , wherein B 1 is 0.90.
4. The cable of claim 1 , wherein Z 2 is 0.58, 0.56, 0.54, 0.52, 0.50, 0.48, 0.46, 0.44, 0.42 or 0.40.
5. The cable of claim 1 , wherein said layer(s) is/are crosslinked and has/have a hot set elongation, with a load of 20 N/cm 2 , which is less than 130%.
6. The cable of claim 1 , wherein the polyethylene is an unsaturated LDPE polymer.
7. The cable of claim 1 , wherein the polyethylene is a copolymer of:
a monomer,
at least one polyunsaturated comonomer, and
zero or one or more other comonomer(s), and
wherein said total amount of vinyl groups (B) present in the polymer composition include vinyl groups originating from said at least one polyunsaturated comonomer.
8. The cable of claim 1 , wherein the polyethylene is a copolymer of a monomer with at least one polyunsaturated comonomer, wherein the polyunsaturated comonomer is a straight carbon chain with at least 8 carbon atoms, at least two non-conjugated double bonds of which at least one is terminal, and at least 4 carbon atoms between the non-conjugated double bonds.
9. The cable of claim 1 , wherein the polyethylene is a copolymer of ethylene and 1,7-octadiene.
10. The cable of claim 1 , wherein the polyethylene is a low density polyethylene (LDPE) homopolymer or copolymer.
11. The cable of claim 1 , wherein B≤B 2 and B 2 is 3.0 and Z 1 ≤Z≤Z 2 , wherein Z 1 is 0.01.
12. The cable of claim 1 , wherein B 1 is 0.95, 1.00, 1.05, 1.10, 1.15, 1.20, 1.25 or 1.30.
13. The cable of claim 1 , wherein the polyethylene contains a total amount of vinyl groups which is P vinyl groups per 1000 carbon atoms, wherein P 1 ≤P≤P 2 and P 1 is 0.89 and P 2 is 3.0.
14. The cable of claim 13 , wherein the polymer composition simultaneously satisfies the following:
P 1 ≤P≤P 2 wherein P 1 is 0.89 and P 2 is 3.0;
Z 1 ≤Z≤Z 2 wherein Z 1 is 0.15 and Z 2 is 0.60; and
wherein the polymer composition has a melt flow rate, MFR 2 , which is A g/10 min and A 1 ≤A≤A 2 wherein A 1 is 0.15 and A 2 is 3.0.
15. The cable of claim 13 , wherein the polymer composition simultaneously satisfies the following:
P 1 ≤P≤P 2 wherein P 1 is 0.9 and P 2 is 1.5;
Z 1 ≤Z≤Z 2 wherein Z 1 is 0.25 and Z 2 is 0.50; and
wherein the polymer composition has a melt flow rate, MFR 2 , which is A g/10 min and A 1 ≤A≤A 2 wherein A 1 is 0.60 and A 2 is 2.5.
16. The cable of claim 1 , wherein the crosslinking agent comprises a peroxide.
17. The cable of claim 1 , wherein the cable is a power cable.
18. A process for producing the cable of claim 1 .
19. The process of claim 18 , wherein said cable is a power cable and wherein said process comprises the steps of:
a 0 ) meltmixing the polymer composition, optionally together with further components; and
a) applying the meltmix obtained from step a 0 ) on a conductor to form at least one cable layer.
20. The process of claim 19 , wherein said cable is a crosslinked power cable and wherein said process further comprises the step of: b) crosslinking the at least one cable layer obtained from step a).