Chabazite zeolite catalysts having low silica to alumina ratios
Disclosed are zeolite catalysts having the CHA crystal structure with a low silica to alumina ratio, as well as articles and systems incorporating the catalysts and methods for their preparation and use. The catalysts can be used to reduce NOx from exhaust gas streams, particularly those emanating from gasoline or diesel engines.
1. A method of making a catalytic article comprising:
ion exchanging an alkali form of a zeolite having the CHA crystal structure containing an initial alkali content with a solution to reduce the alkali content;
calcining the ion exchanged zeolite with the reduced alkali content to provide a calcined zeolite;
subsequently ion exchanging the calcined zeolite with a solution to further reduce the alkali content to provide the zeolite having a mole ratio of silica to alumina of less than about 15 and an alkali content of less than about 1 weight percent,
subsequently, conducting a metal ion exchange with an iron or copper solution to provide a metal promoted zeolite, and
wherein the alkali content is expressed on a weight percent basis in terms of the respective oxides for the alkali present as cations in the zeolite.
2. The method of claim 1 , wherein the solution is an ammonium salt solution.
3. The method of claim 2 , wherein the calcining occurs at a temperature of at least about 350° C. for at least about one hour.
4. The method of claim 1 , wherein the method comprises a sequence of multiple ion exchanges to reduce the alkali content, followed by the calcining step.
5. The method of claim 1 , wherein, after the subsequent ion-exchanging step, the alkali content is less than 0.1 weight percent.
6. The method of claim 1 , wherein, after the subsequent ion-exchanging step, the alkali content is less than 0.05 weight percent.
7. The method of claim 1 , wherein the process further comprises subsequently mixing the zeolite with a second zeolite.
8. The method of claim 7 , wherein the second zeolite has a CHA crystal structure.
9. The method of claim 7 , wherein the second zeolite has a silica to alumina mole ratio exceeding 15.
10. The method of claim 1 , wherein the alkali form of the zeolite having the CHA crystal structure containing the initial alkali content is a potassium form.