High strength long open time polyurethane reactive hot melt
Disclosed is a moisture reactive hot melt adhesive composition prepared from a combination comprising a polyisocyanate, at least one polyether polyol polymer, an acrylic polymer, an inorganic filler and a polyester diol having a structure of Formula 1 or of Formula 2. Formula 1 is: H-[O(CH 2 ) m OOC(CH 2 ) n CO] k -O(CH 2 ) m-OH; m and n are each an even integer; m+n=8; m and n are each independently selected from 2, 4 or 6; k is an integer from 9 to 55; and the polyol of Formula 1 has a number average molecular weight of about 2,000 to about 11,000. Formula 2, a polycaprolactone polyol, is: HO-[(CH 2 ) 5 COO] p R 1 -[OOC(CH 2 ) 5 ] q -OH; R 1 is an initiator such as 1,4′-butanediaol, 1,6′-hexanediol, or ethylene glycol; p is an integer from 0 to 96; q is an integer from 0 to 96; p+q=16 to 96; and the polyol has a number average molecular weight of about 2,000 to about 11,000 or less.
1. A moisture reactive hot melt adhesive composition that is the product of a mixture comprising a polyisocyanate, at least one polyether polyol polymer, an acrylic polymer, from about 10 to about 50% by weight of an inorganic filler, and a having a structure of Formula 2, wherein:
HO-[(CH 2 ) 5 COO] p -R 1 -[OOC(CH 2 ) 5 ] q -OH, wherein:
R 1 is an initiator;
p is an integer from 0 to 96;
q is an integer from 0 to 96;
p+q=16 to 96; and
the polycaprolactone polyol of Formula 2 has a number average molecular weight of from about 2,000 to about 11,000; and
the acrylic polymer is free of active hydrogen groups.
2. The moisture reactive hot melt adhesive composition of claim 1 , wherein R 1 is a residue of a glycol initiator selected from the group consisting of 1,4′-butanediol, 1,6′-hexanediol, ethylene glycol, and any combination thereof.
3. The moisture reactive hot melt adhesive composition of claim 1 , wherein the at least one polyether polyol polymer has a number average molecular weight of from about 2,000 to about 10,000 and is present in an amount of from about 10 to about 35% by weight, based on the total weight of the adhesive composition.
4. The moisture reactive hot melt adhesive composition of claim 1 , wherein the at least one polyether polyol polymer has a number average molecular weight of from about 1,500 to about 6,000 and is present in an amount of from about 15 to about 40% by weight, based on the total weight of the adhesive composition.
5. The moisture reactive hot melt adhesive composition claim 1 , wherein the acrylic polymer has a weight average molecular weight of from 30,000 to 80,000, and is present in an amount of from about 10 to about 40% by weight, based on the total weight of the adhesive composition.
6. The moisture reactive hot melt adhesive composition of claim 1 , wherein the acrylic polymer has a glass transition temperature of from about 35° C. to about 85° C. and a hydroxyl number of less than 8.
7. The moisture reactive hot melt adhesive composition of claim 1 , wherein the polyisocyanate is present in an amount of from about 5 to about 40% by weight, based on the total weight of the adhesive composition.
8. The moisture reactive hot melt adhesive composition of claim 1 , wherein the polyisocyanate comprises 4,4′-methylenebisphenyldiisocyanate.
9. The moisture reactive hot melt adhesive composition of claim 1 , wherein the inorganic filler comprises calcium carbonate.
10. The moisture reactive hot melt adhesive composition of claim 1 , further comprising an additive selected from the group consisting of an additional filler, a plasticizer, a catalyst, a colorant, a rheology modifier, a flame retardant, a UV pigment, a nanofiber, a defoamer, a tackifier, a curing catalyst, an anti-oxidant, an adhesion promoter, a stabilizer, a thixotropic agent, and any mixture thereof.
11. The moisture reactive hot melt adhesive composition of claim 1 , wherein the adhesive composition has an open time of from about 6 to about 10 minutes.
12. The moisture reactive hot melt adhesive composition of claim 1 , wherein the adhesive composition exhibits a green strength of greater than about 120 pounds per square inch (psi) within 30 minutes after application to a substrate.
13. An article of manufacture comprising the moisture reactive hot melt adhesive composition of claim 1 .
14. The moisture reactive hot melt adhesive composition of claim 1 , wherein the adhesive composition consists of:
from about 5 to about 40% by weight of the polyisocyanate;
from about 15 to about 40% by weight of the polyether polyol polymer;
from about 10 to about 40% by weight of the acrylic polymer;
from about 15 to about 50% by weight of the inorganic filler; and
from about 10 to about 35% by weight of the polycaprolactone polyol.
15. The moisture reactive hot melt adhesive composition of claim 1 , wherein the acrylic polymer is free of aminofunctional groups and/or acrylonitrile monomers.
16. The moisture reactive hot melt adhesive composition of claim 1 , wherein the acrylic polymer is a polymer or copolymer formed from acrylates, methacrylates, and any mixture thereof.
17. The moisture reactive hot melt adhesive composition of claim 1 , wherein the at least one polyether polyol polymer comprises a first polypropylene glycol having a number average molecular weight of from about 1500 to about 3000, and a second polypropylene glycol having a number average molecular weight of from about 3000 to about 6000.
18. The moisture reactive hot melt adhesive composition of claim 1 , wherein the adhesive composition:
has an open time of from about 6 to about 10 minutes,
exhibits a green strength of greater than about 120 pounds per square inch (psi) within 30 minutes after application to a substrate,
a yield strength of greater than or equal to 607 psi and/or a tensile strength of greater than or equal to 1415 psi, and
a temperature stability with a storage modulus at 90° C. of equal to or greater than 2.59 E+06.
19. A moisture reactive hot melt adhesive composition that is the product of a mixture comprising a polyisocyanate, at least one polyether polyol polymer, an acrylic polymer, from about 10 to about 50% by weight of an inorganic filler, and a polycaprolactone polyol having a structure of Formula 2, wherein:
Formula 2 is:
HO-[(CH 2 ) 5 COO] p -R 1 -[OOC(CH2) 5 ] q -OH, wherein:
R 1 is an initiator;
p is an integer from 0 to 96;
q is an integer from 0 to 96;
p+q=16 to 96; and
the polycaprolactone polyol of Formula 2 has a number average molecular weight of from about 2,000 to about 11,000; and
the adhesive composition is free of stabilizer and has an open time of between about 6 and about 10 minutes.
20. The moisture reactive hot melt adhesive composition of claim 1 , wherein R 1 is a residue of ethylene glycol.