ADDITIVE MANUFACTURING METHOD AND ASSOCIATED ARTICLE
A method of additive manufacturing an article in the ZX (upright) orientation utilizes a composition including specific amounts of a polycarbonate-polysiloxane and polysiloxane-treated titanium dioxide particles. Although addition of titanium dioxide particles to a plastic composition typically reduces impact strength, articles additively manufactured from this composition exhibit improved impact strength relative to articles manufactured from a corresponding composition lacking the polysiloxane-treated titanium dioxide particles.
1 . A method of additively manufacturing an article in a ZX orientation, the method comprising:
converting a composition from a solid form to a molten form;
extruding the molten form to form a first molten extrusion;
depositing the first molten extrusion in a predetermined pattern to form a first layer;
further extruding the molten form to form a second molten extrusion; and
depositing the second molten extrusion in a predetermined pattern to form a second layer having a lower surface in contact with an upper surface of the first layer;
wherein the composition comprises, based on the total weight of the composition,
10 to 99 weight percent of a polycarbonate-polysiloxane; and
1 to 7.5 weight percent of titanium dioxide-containing particles comprising a polysiloxane.
2 . The method of claim 1 , wherein the polycarbonate-polysiloxane contributes 2 to 8 weight percent polysiloxane to the composition.
3 . The method of claim 1 ,
wherein the composition optionally further comprises a bisphenol A polycarbonate; and
wherein the poly carbonate-polysiloxane and the optional bisphenol A polycarbonate collectively contribute 84 to 97 weight percent bisphenol A carbonate units to the composition.
4 . The method of claim 1 , wherein the titanium dioxide-containing particles have a median equivalent spherical diameter of 0.1 to 0.4 micrometer, determined by laser diffraction according to ISO 13320:2009.
5 . The method of claim 1 ,
wherein the composition comprises 1.5 to 6 weight percent of the titanium dioxide-containing particles;
wherein the poly carbonate-polysiloxane contributes 2 to 6 weight percent of polysiloxane to the composition;
wherein the composition optionally further comprises a bisphenol A polycarbonate; and
wherein the poly carbonate-polysiloxane and the optional bisphenol A polycarbonate collectively contribute 84 to 96.5 weight percent bisphenol A carbonate units to the composition.
6 . An article additively manufactured in a ZX orientation, the article comprising:
at least two contiguous layers;
wherein the at least two contiguous layers comprise a composition comprising, based on the total weight of the composition,
10 to 99 weight percent of a polycarbonate-polysiloxane; and
1 to 7.5 weight percent of titanium dioxide-containing particles comprising a polysiloxane.
7 . The additively manufactured article of claim 6 ,
wherein the additively manufactured article is prepared by fused filament fabrication; and
wherein the additively manufactured article exhibits a notched Izod impact strength value 10 to 50 percent greater than a notched Izod impact strength value of a comparative additively manufactured article prepared from a corresponding composition lacking the titanium dioxide-containing particles, wherein notched Izod impact strength is determined according to ASTM D256-10(2018) at 23° C.
8 . The additively manufactured article of claim 6 , wherein the polycarbonate-polysiloxane contributes 2 to 8 weight percent polysiloxane to the composition.
9 . The additively manufactured article of claim 6 ,
wherein the composition optionally further comprises a bisphenol A polycarbonate; and
wherein the poly carbonate-polysiloxane and the optional bisphenol A polycarbonate collectively contribute 84 to 97 weight percent bisphenol A carbonate units to the composition.
10 . The additively manufactured article of claim 6 , wherein the titanium dioxide-containing particles have a median equivalent spherical diameter of 0.1 to 0.4 micrometer, determined by laser diffraction according to ISO 13320:2009.
11 . The additively manufactured article of claim 6 ,
wherein the composition comprises 1.5 to 6 weight percent of the titanium dioxide-containing particles;
wherein the poly carbonate-polysiloxane contributes 2 to 6 weight percent of polysiloxane to the composition;
wherein the composition optionally further comprises a bisphenol A polycarbonate; and
wherein the poly carbonate-polysiloxane and the optional bisphenol A polycarbonate collectively contribute 84 to 96.5 weight percent bisphenol A carbonate units to the composition.