Method for producing aqueous polyimide precursor solution composition

1. A method for producing an aqueous polyimide precursor solution composition, comprising:

reacting a tetracarboxylic acid component and a diamine component in water containing no organic solvent in a presence of an imidazole to form a polyamic acid comprising a repeating unit represented by the following formula (1),

wherein,

the polyamic acid and the imidazole are dissolved in the water,

an amount of the imidazole is 1.6 mole or more per mole of the tetracarboxylic acid component,

the tetracarboxylic acid component comprises at least one selected from the group consisting of an aromatic tetracarboxylic dianhydride containing no fluorine group, an aliphatic tetracarboxylic dianhydride, and an aromatic tetracarboxylic dianhydride containing a fluorine group; the aromatic tetracarboxylic dianhydride containing no fluorine group being selected from the group consisting of 3,3′,4,4′-biphenyltetracarboxylic dianhydride, 2,3,3′,4′-biphenyltetracarboxylic dianhydride, 2,2′,3,3′-biphenyltetracarboxylic dianhydride, 4,4′-oxydiphthalic dianhydride, diphenylsulfone tetracarboxylic dianhydride, p-terphenyl tetracarboxylic dianhydride, and m-terphenyl tetracarboxylic dianhydride, and

the diamine component comprises at least one selected from the group consisting of an aromatic diamine containing no fluorine group and having a solubility in water at 25° C. of 0.1 g/L or more, and an aromatic diamine containing a fluorine group, and

wherein,

more than 50 mol % of the tetracarboxylic acid component is the aromatic tetracarboxylic dianhydride containing no fluorine group, and less than 50 mol %, including 0 mol %, of the tetracarboxylic acid component is the aliphatic tetracarboxylic dianhydride, and/or the aromatic tetracarboxylic dianhydride containing a fluorine group, and

more than 50 mol % of the diamine component is the aromatic diamine containing no fluorine group and having a solubility in water at 25° C. of 0.1 g/L or more, and less than 50 mol %, including 0 mol %, of the diamine component is the aromatic diamine containing a fluorine group, and

a combination of only the aromatic tetracarboxylic dianhydride containing no fluorine group, and only the aromatic diamine containing no fluorine group is excluded,

wherein

A represents a tetravalent group derived from the tetracarboxylic acid component and B represents a divalent group derived from the diamine component.

2. The method for producing an aqueous polyimide precursor solution composition as claimed in claim 1 , wherein the imidazole is selected from the group consisting of 1,2-dimethylimidazole, 2-ethyl-4-methylimidazole, 4-ethyl-2-methylimidazole, and 1-methyl-4-ethylimidazole.

3. The method for producing an aqueous polyimide precursor solution composition as claimed in claim 1 , wherein the aqueous polyimide precursor solution composition has an inherent viscosity of 0.4 or more.

4. A method for producing an electrode, comprising: producing the aqueous polyimide precursor solution composition according to the method of claim 1 ; and

mixing the aqueous polyimide precursor solution composition and at least an electrode active material to form an electrode mixture paste,

applying the electrode mixture paste onto a current collector, and

heating the electrode mixture paste to remove a solvent and effect imidization.

5. A method for producing a flexible device which is a display device or a light-receiving device, comprising: producing the aqueous polyimide precursor solution composition according to the method of claim 1 ; and

applying the aqueous polyimide precursor solution composition onto a carrier substrate, and then heating the composition to form a solid polyimide resin film;

forming a circuit on the polyimide resin film; and

separating the polyimide resin film on which the circuit is formed from the carrier substrate.

6. A method for producing an aqueous polyimide precursor solution composition, comprising:

reacting a tetracarboxylic acid component and a diamine component in water containing no organic solvent in a presence of an imidazole at 50° C. or higher and 100° C. or lower to form a polyamic acid comprising a repeating unit represented by the following formula (1),

wherein,

the polyamic acid and the imidazole are dissolved in the water,

an amount of the imidazole is 1.6 mole or more per mole of the tetracarboxylic acid component,

the tetracarboxylic acid component comprises at least one selected from the group consisting of an aromatic tetracarboxylic dianhydride containing no fluorine group, an aliphatic tetracarboxylic dianhydride, and an aromatic tetracarboxylic dianhydride containing a fluorine group, and

the diamine component comprises at least one selected from the group consisting of an aromatic diamine containing no fluorine group and having a solubility in water at 25° C. of 0.1 g/L or more, and an aromatic diamine containing a fluorine group, and

wherein,

more than 50 mol % of the tetracarboxylic acid component is the aromatic tetracarboxylic dianhydride containing no fluorine group, and less than 50 mol %, including 0 mol %, of the tetracarboxylic acid component is the aliphatic tetracarboxylic dianhydride, and/or the aromatic tetracarboxylic dianhydride containing a fluorine group, and

more than 50 mol % of the diamine component is the aromatic diamine containing no fluorine group and having a solubility in water at 25° C. of 0.1 g/L or more, and less than 50 mol %, including 0 mol %, of the diamine component is the aromatic diamine containing a fluorine group, and

a combination of only the aromatic tetracarboxylic dianhydride containing no fluorine group, and only the aromatic diamine containing no fluorine group is excluded,

wherein

A represents a tetravalent group derived from the tetracarboxylic acid component and B represents a divalent group derived from the diamine component.