Composition and process for pelletizing carbon-based materials for proppant and industrial applications
A method for producing an electrically-conductive pellet includes reducing a size of a first material. The method also includes wetting the first material to produce a first slurry. The method also includes introducing the first slurry into a fluidizer to produce a first pellet. The method also includes reducing a size of a second material. The second material is an electrically-conductive material. The method also includes wetting the second material to produce a second slurry. The method also includes applying the second slurry to the first pellet.
1. A method for producing an electrically-conductive pellet, comprising:
reducing a size of a first material, wherein the first material is alumina, silica, kaolin ore, or bauxite ore or combinations thereof;
wetting the first material to produce a first slurry;
introducing the first slurry into a fluidizer to produce a first pellet;
reducing a size of a second material, wherein the second material comprises an electrically-conductive material, wherein the electrically-conductive material comprises coke;
wetting the second material to produce a second slurry; and
applying the second slurry to the first pellet to provide an electrically conductive pellet, and
calcining the electrically-conductive pellet to provide a calcined electrically-conductive pellet comprising a core that is a calcined first material and a shell comprising calcined coke.
2. The method of claim 1 , wherein the second material comprises coke, metal, graphite, or a combination thereof.
3. The method of claim 1 , wherein the second material comprises a blend of clay with petroleum coke.
4. The method of claim 1 , wherein an average cross-sectional length of the electrically-conductive pellet is from about 200 μm to about 4000 μm.
5. The method of claim 1 , wherein a bulk density of the electrically-conductive pellet is from about 0.3 g/cm 3 to about 2.0 g/cm 3 .
6. The method of claim 1 , wherein an electrical conductivity of the electrically-conductive pellet is from about 100 S/m to about 3000 S/m.
7. The method of claim 1 , further comprising:
reducing a size of a third material, wherein the third material comprises a combination of the first material and the second material; and
wetting the third material to produce a third slurry.
8. The method of claim 7 , further comprising applying the third material to the first pellet before the second slurry is applied such that the third material is positioned at least partially between the first pellet and the second material.
9. The method of claim 1 , further comprising:
reducing a size of a third material, wherein the third material comprises a combination of the first material and the second material;
wetting the third material to produce a third slurry;
applying the third material to the first pellet before the second slurry is applied such that the third material is positioned at least partially between the first pellet and the second material; and
calcining the electrically-conductive pellet after the second and third materials have been applied to the first pellet, and wherein:
an average cross-sectional length of the electrically-conductive pellet is from about 300 μm to about 2000 μm,
a bulk density of the electrically-conductive pellet is from about 0.5 g/cm 3 to about 1.6 g/cm 3 , and
an electrical conductivity of the electrically-conductive pellet is from about 500 S/m to about 2000 S/m.