Cladded amorphous metal products
An embodiment relates to a cladded composite comprising a cladding layer of a bulk metallic glass and a substrate; wherein the bulk metallic glass comprises approximately 0% crystallinity, approximately 0% porosity, less than 50 MPa thermal stress, approximately 0% distortion, approximately 0 inch heat affected zone, approximately 0% dilution, and a strength of about 2,000-3,500 MPa.
1. A cladded composite comprising a substrate and a cladding layer comprising a bulk metallic glass on the substrate; wherein the bulk metallic glass comprises 0-10% crystallinity, no porosity, less than 50 MPa thermal stress, no distortion, no heat affected zone, no dilution, and a bond strength of about 2,000-3,500 MPa;
wherein the bulk metallic glass comprises a Zr based alloy comprising Cu; wherein the substrate comprises steel, aluminum or titanium.
2. The cladded composite of claim 1 , wherein the bulk metallic glass further comprises Ni and Al.
3. The cladded composite of claim 2 , wherein the cladding layer comprises a foil having a foil thickness of about 20-300 μm and the cladding layer has a thickness of about 0.02 mm to 5 mm.
4. The cladded composite of claim 3 , wherein the cladding layer comprises multiple sheets of the foil.
5. The cladded composite of claim 1 , wherein the cladded composite comprises a bond layer between the substrate and the cladding layer.
6. The cladded composite of claim 1 further comprising an interlayer, wherein the interlayer and the substrate has a disjoint crystal of less than 1 micron in size.
7. The cladded composite of claim 1 , wherein the bulk metallic glass comprises no crystallinity and no thermal stress.
8. The cladded composite of claim 1 , wherein the bulk metallic glass comprises a ZrCuNiAl alloy.
9. The cladded composite of claim 8 , wherein the ZrCuNiAl alloy comprises Zr at about 75.72 wt. %, Cu at about 4.2 wt. %, Ni at about 2.5 wt. % and Al at about 2.58 wt. %.
10. The cladded composite of claim 1 , wherein the bulk metallic glass comprises a ZrTiNiCuHf alloy.
11. The cladded composite of claim 10 , wherein the ZrTiNiCuHf alloy comprises Zr at about 64.5 wt. %, Ti at about 14.7 wt. %, Ni at about 12.6 wt. %, Cu at about 7 wt. % and Hf at about 1.2 wt. %.
12. The cladded composite of claim 1 , wherein the bulk metallic glass comprises a ZrCuNiAlTi alloy.
13. The cladded composite of claim 1 , wherein the ZrCuNiAlTi alloy comprises Zr at about 65.7 wt. %, Cu at about 15.5 wt. %, Ni at about 11.7 wt. %, Al at about 3.7 wt. %, and Ti at about 3.3 wt. %.