Absorbent laminated material
Absorbent laminated materials that include two spunbond nonwoven layers with a cellulose layer arranged in between the spunbond nonwoven layers are disclosed. The different layers of the absorbent laminated material are bonded through an ultrasonic treatment, and can further undergo an embossing step. In addition, the absorbent laminated materials may be used as disposable wiping products, among other applications.
1. A method of making an absorbent laminated material, the method comprising:
providing a first spunbond nonwoven layer having a basis weight of from about 1 gsm to about 30 gsm and comprising a thermoplastic polymer, a second spunbond nonwoven layer having a basis weight of from about 1 gsm to about 30 gsm and comprising a thermoplastic polymer, and a cellulose layer having a basis weight of from about 10 gsm to about 100 gsm;
arranging the cellulose layer such that the cellulose layer is between the first spunbond nonwoven layer and second spunbond nonwoven layers, wherein the cellulose layer extends continuously between the first spunbond nonwoven layer and the second spunbond nonwoven layer; and
performing an ultrasonic treatment on the arranged layers to provide an absorbent laminated material,
wherein the cellulose layer is free of thermoplastic fibers and has a peel strength of greater than 10 grams/inch.
2. The method of claim 1 , wherein the cellulose layer is provided at a ratio of about 4:1 to about 1:2 relative to the weight of the first spunbond nonwoven layer and second spun bond nonwoven layers combined.
3. The method of claim 1 , wherein the cellulose layer is formed by a paper-making process or by an air forming process.
4. The method of claim 1 , wherein the method comprises a single ultrasonic treatment.
5. The method of claim 1 , wherein the method further comprises embossing the absorbent laminated material.
6. The method of claim 1 , wherein the absorbent laminated material has an absorbency of greater than 300% relative to the dry weight of the absorbent laminated material.
7. The method of claim 1 , wherein the absorbent laminated material comprises layers having the same length and width.
8. A method of making an absorbent laminated material, the method comprising:
providing a first spunbond nonwoven layer having a basis weight of from about 1 gsm to about 30 gsm and comprising a thermoplastic polymer, a second spunbond nonwoven layer having a basis weight of from about 1 gsm to about 30 gsm and comprising a thermoplastic polymer, and a cellulose layer having a basis weight of from about 10 gsm to about 100 gsm;
arranging the cellulose layer such that the cellulose layer is between the first spunbond nonwoven layer and second spunbond nonwoven layers; and
performing an ultrasonic treatment on the arranged layers to provide an absorbent laminated material,
wherein the cellulose layer is free of bonding agents and has a peel strength of greater than 10 grams/inch, and
wherein the absorbent laminated material has a cross-direction wet tensile strength between 600 grams to 1200 grams.