Aerosol primer composition and method of use
An aerosol primer composition includes a film forming component and a propellant component. The film forming component includes (by weight of the composition): (a) at least one of a polyurethane and alkyd from about 10% to about 20%, (b) cellulosic particles from about 2% to about 5%, and (c) an aqueous solvent system from about 20% to about 40%. The propellant component includes dimethyl ether. The aerosol primer composition can be stored within a spray assembly and the propellant component can be configured to pressurize the film forming component for dispensing from the spray assembly as an aerosol. The aerosol primer composition can be used to prime a substrate to be painted or stained.
1. An aerosol primer composition, comprising:
a film forming component comprising (by weight of the composition):
(a) at least one of a polyurethane and alkyd from about 10% to about 20%,
(b) cellulosic particles from about 2% to about 5%, and
(c) an aqueous solvent system from about 20% to about 40%; and
a propellant component comprising dimethyl ether.
2. The aerosol primer composition of claim 1 , wherein a ratio of an amount of the film forming component to an amount of the propellant component is from about 60:40 to about 70:30 (by weight).
3. The aerosol primer composition of claim 1 , wherein the cellulosic particles comprise at least one of wood particles, wood flour, sawdust, and nut shell particles.
4. The aerosol primer composition of claim 1 , wherein the cellulosic particles comprise a particle diameter capable of passing through a filter pore having a pore diameter of about 160 micrometers to about 220 micrometers.
5. The aerosol primer composition of claim 1 , wherein the film forming component further comprises at least one component selected from (by weight of the composition):
a rheology additive from about 0.05% to about 0.5%,
a dispersing agent from about 0.3% to about 1%,
a mineral filler from about 2% to about 5%,
a corrosion inhibitor from about 0.05% to about 0.5%, and
a pigment from about 0.01% to about 6%.
6. The aerosol primer composition of claim 1 , wherein the aqueous solvent system comprises water or a combination of water and isopropyl alcohol.
7. The aerosol primer composition of claim 1 , wherein the film forming component comprises a viscosity of about 50 centipoise to about 150 centipoise.
8. The aerosol primer composition of claim 1 , wherein the at least one of a polyurethane and alkyd is a polyurethane, and further wherein the aqueous solvent system comprises water and isopropyl alcohol.
9. The aerosol primer composition of claim 1 , wherein the film forming component consists essentially of (by weight of the composition):
(a) a polyurethane from about 10% to about 20%,
(b) cellulosic particles from about 2% to about 5%,
(c) an aqueous solvent system consisting of water and isopropyl alcohol from about 20% to about 40%, and
(d) at least one component selected from:
a rheology additive from about 0.05% to about 0.5%,
a dispersing agent from about 0.3% to about 1%,
a mineral filler from about 2% to about 5%,
a corrosion inhibitor from about 0.05% to about 0.5%, and
a pigment from about 0.01% to about 6%.
10. A method of priming a substrate to be painted or stained, comprising:
dispensing a primer composition onto a surface of the substrate from a pressurized container, wherein the primer composition comprises:
a film forming component comprising (by weight of the composition):
(a) at least one of a polyurethane and alkyd from about 10% to about 20%,
(b) cellulosic particles from about 2% to about 5%, and
(c) an aqueous solvent system from about 20% to about 40%; and
a propellant component comprising dimethyl ether,
wherein the dispensing is conducted such that the propellant evaporates as the primer composition is dispensed from the pressurized container and the film forming component defines a coating on the surface of the substrate.
11. The method of claim 10 , wherein the substrate comprises one of a polymer, glass, masonry, wood, ceramic, stone, fiberglass, gypsum board, particle board, fiber board, and metal.
12. The method of claim 10 , further comprising:
forming a pattern in the coating comprising the film forming component.
13. The method of claim 10 , further comprising:
applying one of a paint, wood stain, and masonry stain on the coating.
14. The method of claim 10 , wherein the cellulosic particles comprise at least one of wood particles, wood flour, sawdust, and nut shell particles.
15. The method of claim 10 , wherein the film forming component further comprises at least one component selected from (by weight of the composition):
a rheology additive from about 0.05% to about 0.5%,
a dispersing agent from about 0.3% to about 1%,
a mineral filler from about 2% to about 5%,
a corrosion inhibitor from about 0.05% to about 0.5%, and
a pigment from about 0.01% to about 6%.
16. A spray assembly for an aerosol primer composition, comprising:
a container defining a chamber configured to hold an aerosol primer composition at a pressure above ambient pressure;
a dispensing spray outlet fluidly coupled with the chamber for dispensing the aerosol primer composition from the chamber; and
an aerosol primer composition comprising:
a film forming component comprising (by weight of the composition):
(a) at least one of a polyurethane and alkyd from about 10% to about 20%,
(b) cellulosic particles from about 2% to about 5%, and
(c) an aqueous solvent system from about 20% to about 40%; and
a propellant component comprising dimethyl ether,
wherein the propellant component comprises a propellant selected to pressurize the film forming component within the chamber.
17. The spray assembly of claim 16 , wherein a ratio of an amount of the film forming component to an amount of the propellant component is from about 60:40 to about 70:30 (by weight).
18. The spray assembly of claim 16 , wherein the cellulosic particles comprise at least one of wood particles, wood flour, sawdust, and nut shell particles.
19. The spray assembly of claim 16 , wherein the cellulosic particles comprise a particle diameter capable of passing through a filter pore having a pore diameter of about 160 micrometers to about 220 micrometers.
20. The spray assembly of claim 16 , wherein the film forming component comprises a viscosity of about 50 centipoise to about 150 centipoise.