Ultra-high strength aluminum alloy products and methods of making the same
Provided herein are ultra-high strength aluminum alloys and products prepared therefrom, along with methods of processing the ultra-high strength aluminum alloys. The aluminum alloys described herein are high solute alloys, including significant amounts of zinc (Zn), magnesium (Mg), copper (Cu), and other elements in addition to aluminum. The aluminum alloys described herein are amenable to post-aging processing without cracking.
1. An aluminum alloy for a rolled aluminum alloy product, the aluminum alloy comprising 7.0 to 11.0 wt. % Zn, 2.2 to 3.0 wt. % Mg, 1.2 to 2.5 wt. % Cu, less than 0.10 wt. % Mn, up to 0.25 wt. % Cr, up to 0.20 wt. % Si, 0.05 to 0.30 wt. % Fe, up to 0.10 wt. % Ti, 0.05 to 0.25 wt. % Zr, up to 0.25 wt. % Sc, up to 0.15 wt. % impurities, and Al,
wherein the aluminum alloy comprises a yield strength greater than 700 MPa when in a T9 temper;
wherein a combined content of Zr and Sc ranges from 0.10 to 0.25 wt. %;
wherein the combined amount of Zn, Mg, and Cu is from 11 wt. % to 16 wt. %; and
wherein a mass fraction of Mg 2 Zn in the aluminum alloy microstructure is at least 10%.
2. The aluminum alloy of claim 1 , comprising 7.1 to 11.0 wt. % Zn, 2.2 to 3.0 wt. % Mg, 1.6 to 2.5 wt. % Cu, 0 to 0.09 wt. % Mn, up to 0.25 wt. % Cr, up to 0.20 wt. % Si, 0.05 to 0.30 wt. % Fe, up to 0.10 wt. % Ti, 0.05 to 0.25 wt. % Zr, up to 0.20 wt. % Sc, up to 0.15 wt. % impurities, and Al.
3. The aluminum alloy of claim 1 , comprising 8.3 to 10.7 wt. % Zn, 2.2 to 2.6 wt. % Mg, 2.0 to 2.5 wt. % Cu, 0.01 to 0.09 wt. % Mn, 0.01 to 0.20 wt. % Cr, 0.01 to 0.20 wt. % Si, 0.05 to 0.25 wt. % Fe, 0.01 to 0.05 wt. % Ti, 0.05 to 0.20 wt. % Zr, up to 0.10 wt. % Sc, up to 0.15 wt. % impurities, and Al.
4. The aluminum alloy of claim 1 , comprising 8.5 to 10.5 wt. % Zn, 2.2 to 2.5 wt. % Mg, 2.0 to 2.4 wt. % Cu, 0.02 to 0.06 wt. % Mn, 0.03 to 0.15 wt. % Cr, 0.01 to 0.10 wt. % Si, 0.08 to 0.20 wt. % Fe, 0.02 to 0.05 wt. % Ti, 0.10 to 0.15 wt. % Zr, up to 0.10 wt. % Sc, up to 0.15 wt. % impurities, and Al.
5. The aluminum alloy of claim 1 , wherein the aluminum alloy has a ratio of Cu to Mg from 1:1 to 1:2.5; a ratio of Cu to Zn from about 1:3 to about 1:8; and/or a ratio of Mg to Zn from about 1:2 to about 1:6.
6. The aluminum alloy of claim 1 , wherein a combined amount of Mn and Cr is at least 0.06 wt. %.
7. The aluminum alloy of claim 1 , wherein the aluminum alloy comprises Sc-containing dispersoids, Zr-containing dispersoids, or dispersoids containing Sc and Zr.
8. The aluminum alloy of claim 1 , further comprising up to 0.1 wt. % Er, wherein the aluminum alloy comprises Er-containing dispersoids.
9. The aluminum alloy of claim 1 , further comprising up to 0.1 wt. % Hf, wherein the aluminum alloy comprises Hf-containing dispersoids.
10. An aluminum alloy product, comprising the aluminum alloy according to claim 1 .
11. The aluminum alloy product of claim 10 , wherein the aluminum alloy product comprises a sheet having a gauge of less than about 4 mm.
12. The aluminum alloy product of claim 10 , wherein the aluminum alloy product has a yield strength of about 700 MPa or greater when in a T9 temper and/or has a total elongation of at least about 2% when in a T9 temper.
13. The aluminum alloy product of claim 10 , wherein the aluminum alloy product has a yield strength of about 600 MPa or greater when in a T6 temper and/or has a total elongation of at least about 7% when in a T6 temper.