Seal validation with chemical pre-treatment

1. A method, comprising:

establishing an Arrhenius relationship between a material response of a material exposed to a test fluid and an aging temperature of the material, based at least in part on experimental results of testing a plurality of material samples made of the material;

determining, based at least in part on the Arrhenius relationship, a pre-treatment time and a pre-treatment temperature that approximates a seal end-of-life condition;

pre-treating a seal by exposing the seal to the test fluid at the determined pre-treatment temperature for the determined pre-treatment time, the seal having at least in part a same material composition as the plurality of material samples; and

after pre-treating the seal, performing one or more validation tests on the pre-treated seal.

2. The method of claim 1 , wherein determining the pre-treatment time and the pre-treatment temperature comprises:

determining or estimating a thermal half-life of the material response based on the Arrhenius relationship; and

solving the equation:

t

P

⁢

T

=

t

A

⁢

p

⁢

p

×

2

⋀

(

T

P

⁢

T

-

T

A

⁢

p

⁢

p

h

)

,

wherein:

h is the thermal half-life;

t PT is the pre-treatment time;

t App is an estimated lifetime of the seal;

T PT is the pre-treatment temperature; and

T App is an application temperature at which the seal is expected to be exposed during an application.

3. The method of claim 2 , wherein t PT is a predetermined amount of time available for pre-treating the seal.

4. The method of claim 2 , wherein determining the thermal half-life comprises:

setting a time t 1 equal to a predetermined t PT value or t App value;

determining a temperature T 1 corresponding to t 1 according to the Arrhenius relationship;

setting a time t 2 equal to t 1 /2;

determining a temperature T 2 corresponding to t 2 according to the Arrhenius relationship; and

subtracting T 2 from T 1 .

5. The method of claim 4 , wherein the thermal half-life (h) is an effective thermal half-life, wherein determining the effective thermal half-life comprises:

determining a first thermal half-life using a time t 1 equal to a predetermined t PT value;

determining a second thermal half-life using a time t 1 equal to a t App value; and

averaging the first thermal half-life and the second thermal half-life.

6. The method of claim 2 , wherein the thermal half-life is estimated, and wherein t PT is determined based on the estimated thermal half-life.

7. The method of claim 6 , wherein the thermal half-life is estimated to be a value between −5 and −15 wherein T 1 and T 2 are in Kelvin.

8. The method of claim 6 , further comprising determining t PT based on the equation

h=T 1 −T 2 , where:

T 1 is a temperature corresponding to t PT according to the Arrhenius relationship; and

T 2 is a temperature corresponding to t PT /2 according to the Arrhenius relationship.

9. The method of claim 1 , further comprising:

providing the plurality of material samples;

exposing each of the material samples to one or more portions of the test fluid; and

testing the plurality of material samples after the material samples are exposed to the test fluid, wherein the Arrhenius relationship is established based on the results of the testing.

10. The method of claim 9 , wherein testing the plurality of material samples comprises:

exposing a first group of material samples of the plurality of material samples to a first portion of the test fluid at a first temperature;

exposing a second group of material samples of the plurality of material samples to a second portion of the test fluid at a second temperature; and

testing the first group of material samples and the second group of material samples.

11. The method of claim 10 , wherein:

testing the first group of material samples comprises:

removing different material samples of the first group of material samples from the test fluid at different times; and

performing a mechanical test on each of the material samples of the first group of material samples upon removing the material sample from the test fluid; and

testing the second group of material samples comprises:

removing different material samples of the second group of material samples from the test fluid at different times; and

performing a mechanical test on each of the material samples of the second group of material samples upon removing the material sample from the test fluid.

12. The method of claim 11 , wherein establishing the Arrhenius relationship comprises:

fitting a first curve to a mechanical response of the first group of material samples with respect to time that the material samples were aged in the test fluid;

fitting a second curve to a mechanical response of the second group of material samples with respect to time that the material samples were aged in the test fluid;

calculating a first time to failure of material samples aged at the first temperature based on the first curve;

calculating a second time to failure of material samples aged at the second temperature based on the second curve; and

establishing the Arrhenius relationship by fitting a linear curve to two points corresponding to (ln(TtF 1 ), 1/T 1 ) and (ln(TtF 2 ), 1/T 2 ), wherein

T 1 is the first temperature;

T 2 is the second temperature;

TtF 1 is the first time to failure; and

TtF 2 is the second time to failure.

13. The method of claim 9 , wherein testing the plurality of material samples further comprises:

exposing each of the material samples to the one or more portions of the test fluid at a temperature T 1 ;

removing different material samples of the plurality of material samples from the test fluid at different times; and

performing a mechanical test on each of the material samples upon removing the material sample from the test fluid.

14. The method of claim 13 , wherein establishing the Arrhenius relationship comprises:

fitting a curve to a mechanical response of the plurality of material samples with respect to time that the material samples were aged in the test fluid;

calculating a first time to failure (TtF 1 ) of the material samples aged at the temperature T 1 based on the curve;

estimating a thermal half-life of the material response;

calculating a second time to failure (TtF 2 ) equal to TtF 1 minus the estimated thermal half-life; and

establishing the Arrhenius relationship by fitting a linear curve to two points corresponding to (ln(TtF 1 ), 1/T 1 ) and (ln(TtF 2 ), 1/T 2 ), wherein T 2 =T 1 /2.

15. The method of claim 14 , wherein the thermal half-life is estimated to be a value between −5 and −15 wherein T 1 and T 2 are in Kelvin.

16. The method of claim 1 , wherein the test fluid has a composition expected to be encountered by a seal located in subsea or subterranean equipment during a subsea or subterranean application.

17. The method of claim 1 , wherein the material of the material samples and the seal is nonmetallic.

18. The method of claim 1 , further comprising:

determining whether to use a new seal having a same material composition as the seal in equipment within a subsea or subterranean environment based on results of the one or more validation tests performed on the pre-treated seal; and

upon determining to use the new seal, positioning the equipment with the new seal into the subsea or subterranean environment; and

operating the equipment in the subsea or subterranean environment.

19. The method of claim 1 , wherein the one or more validation tests comprise a testing standard wherein the pre-treated seal is cycled through exposure to various pressures and temperatures in a predetermined sequence.

20. The method of claim 1 , wherein the one or more validation tests comprise exposing the pre-treated seal to a second test fluid and an elevated pressure.