Bone gel sheet composition and method of manufacture
A bone gel composition consists of cortical bone. The cortical bone is made from cut pieces freeze-dried then ground into particles and demineralized then freeze-dried. A volume of the particles is placed in a solution of sterile water to create a mixture, the water volume being at least twice the particle volume, the mixture is autoclaved under heat and pressure to form a gelatin, the resulting bone gel is formed into sheets having a thickness (t).
1. A method of making a bone gel composition consisting of cortical bone comprises the steps of: preparing cortical bone by cutting the cortical bone into pieces, freeze-drying the pieces and then grinding into particles of a size up to 125 microns and demineralizing the ground particles and then freeze-drying the demineralized ground particles to form DBM particles;
autoclaving a volume of the DBM particles mixed with sterile water in a 1:2 ratio by volume for a predetermined time at a pre-set temperature and pressure to form a gelatin, the gelatin consisting of the volume of the DBM particles and the sterile water;
cooling the gelatin to form a bone gel;
forming the bone gel into sheets of bone gel of a thickness (t), the thickness (t) being in the range of 1.0 to 10.0 mm;
cutting the sheets of bone gel to a desired circular, semi-circular or polygonal shape; and
freezing or packaging the cut sheets of bone gel, wherein the cut sheets of bone gel are frozen either before or after packaging, wherein the sheets of bone gel when cut into different shapes with no visible cracks maintains the cut shape while immersed in normal saline or water for a minimum of one minute.
2. The method of making a bone gel composition of claim 1 wherein the polygonal shape is a square or rectangle.
3. The method of making a bone gel composition of claim 2 wherein the polygonal shape is a rectangle.
4. The method of making a bone gel composition of claim 1 wherein the thickness (t) is in the range of 2 to 3 mm.
5. The method of making a bone gel composition of claim 3 wherein the rectangle has a predetermined width and a predetermined length.
6. The method of making a bone gel composition of claim 1 wherein the bone gel sheet is frozen at −20 to −80 degrees C.
7. The method of making a bone gel composition of claim 1 wherein the cortical bone has the cut pieces having a width, a length and a thickness in the range of 1 to 4 mm.