Glueless dustless composite flooring material system
A glueless dustless composite flooring material system providing PVC-based flooring having waterproof layers providing different qualities of hardness, wear-resistance, sound deadening, and decorative patterns, avoiding the use of moisture-susceptible compressed cellulose-based filler, with layers fused together, avoiding the manufacturing complexity and delamination risks of using glue or adhesive, with a quickly-cured, UV-cured top coating providing long-lasting high performance and shortening and simplifying the manufacturing, which can be done in a sheet-form, essentially continuous-run manner, with an ability to quickly and simply change the optional design printing and texturing produced, and having an optional underlayment layer.
1. A glueless dustless composite flooring material product having a nominal top and bottom direction, the glueless dustless composite flooring material comprising:
(i) a waterproof flooring base layer comprising a PVC resin mixture free of compressed cellulose material and adhesive and having compatible materials adapted to provide desired qualities in said flooring base layer, in use, said PVC resin mixture formable by mixing, fusing, cooling, delivering, extruding, co-extruding, and mold forming, said PVC resin mixture comprising:
(a) 50 kg polyvinyl chloride (PVC);
(b) 100-200 kg 300-1000 mesh calcium carbonate;
(c) 3-5 kg calcium/zinc heat stabilizer;
(d) 2.5-5 kg elastomer;
(e) 1-4 kg acrylic polymer modifier;
(f) 0.3-0.6 kg internal lubricant; and
(g) 0.4-1.5 kg high melting point polymer;
(ii) a waterproof flooring face layer comprising a decorative face sub-layer secured atop the flooring base layer and a wearing face sub-layer secured atop the decorative face layer, the decorative face sub-layer comprising a PVC decorative polymer film and the wearing face sub-layer comprising a PVC wear-resistant film;
wherein said flooring face layer is fused by hot-melt overlaying to a top face of said flooring base layer and forms a unitary base-and-face subassembly; and
(iii) a waterproof flooring coating layer comprising a UV-curable plastic resin and secured atop the wearing face layer, the flooring coating layer being formable by coating a top face of said base-and-face subassembly with at least one UV-curable plastic resin;
wherein said base-and-face assembly and said flooring coating layer are fusible together and form a waterproof finished-large-sheet assembly;
wherein said finished-large-sheet assembly is profile-processable to desired size and shape, yielding multiple flooring segments of waterproof floor covering free of water-based materials.
2. The flooring material of claim 1 , wherein said flooring base layer comprises a first extruded base sub-layer and a second co-extruded base sub-layer fused atop the first base sub-layer, the first and the second base layers being mold formable.
3. The flooring material of claim 1 , further comprising (iv) an underlayment layer.
4. The flooring material of claim 1 , wherein said PVC decorative polymer film further comprises a colored film.
5. The flooring material of claim 1 , wherein said PVC decorative polymer film further comprises an applied decorative pattern.
6. The flooring material of claim 1 , further comprising a textured surface embossed upon said base-and-face assembly.
7. The flooring material of claim 1 , wherein said PVC wear resistant polymer film is transparent.
8. The flooring material of claim 1 , wherein said flooring coating layer is transparent.
9. The flooring material of claim 1 , wherein said flooring coating layer further comprises a gritty particulate material.
10. The flooring material of claim 1 , wherein said flooring coating layer further comprises aluminum oxide.
11. The flooring material of claim 1 , wherein said PVC resin mixture further comprises (h) 0.2-0.3 kg high density polyethylene oxide.
12. The flooring material of claim 1 , wherein said (d) 2.5-5 kg elastomer is a chlorinated polyethylene elastomer (CPE).
13. The flooring material of claim 1 , wherein said flooring coating layer further comprises a UV-curable primer and at least one UV-curable top coat.
14. The flooring material of claim 1 , wherein said UV-curable plastic resin is curable by exposure to Mercury (Hg) or Gallium (Ga) lamps.
15. The flooring material of claim 1 , wherein said flooring base layer is formable by heating the mixture to 110-130° C. while stirring at a high speed.
16. The flooring material of claim 1 , wherein hot-melt overlaying of said flooring face layer and said flooring base layer are fusible by passing the flooring base and the face layers through at least one set of heated rollers.
17. The flooring material of claim 1 , wherein extrusion of said flooring base layer further comprises extrusion using at least an 85 mm-diameter screw at a temperature of 160-250° C.
18. A glueless dustless composite flooring material product having a nominal top and bottom direction, the glueless dustless composite flooring material comprising:
(i) a waterproof flooring base layer comprising a PVC resin mixture free of compressed cellulose material and adhesive, said PVC resin mixture having compatible materials adapted to provide desired qualities in said flooring base layer, in use, said PVC resin mixture formable by mixing, fusing, cooling, delivering, co-extruding, and mold forming, and said PVC resin mixture comprising, by weight, between 19% and 25% polyvinylchloride, between 50% and 75% calcium carbonate, between 1.4% and 1.9% calcium/zinc heat stabilizer, between 1.2% and 1.9% elastomer, between 0.5% and 1.5% acrylic polymer modifier, between 0.1% and 0.3% internal lubricant, and between 0.2% and 0.7% high melting point polymer;
(ii) a waterproof flooring face layer comprising a decorative face sub-layer secured atop the flooring base layer and a wearing face sub-layer secured atop said decorative face layer, the decorative face sub-layer comprising a PVC decorative film with an applied decorative pattern, and the wearing face sub-layer comprising a PVC wear-resistant film;
wherein said flooring face layer is fused by hot-melt overlaying to a top face of said flooring base layer and forms a unitary base-and-face subassembly; and
(iii) a waterproof flooring coating layer comprising a UV-curable plastic resin and secured atop the wearing face layer, the flooring coating layer being formable by coating a top face of said base-and-face subassembly with at least one UV-curable plastic resin;
wherein layers of said base-and-face assembly and said flooring coating layer are fusible together and form a waterproof finished-large-sheet assembly;
wherein said finished-large-sheet assembly is profile-processable to desired size and shape, yielding multiple flooring segments of waterproof floor covering free of water-based material.
19. The flooring material of claim 18 , wherein said PVC resin mixture further comprises, by weight, between 0.1% and 0.2% high density polyethylene oxide.