Closed cell foams including poly-4-hydroxybutyrate and copolymers thereof
Methods to produce substantially closed cell foams with densities less than 0.75 g/cm 3 , and more preferably less than 0.5 g/cm 3 , without substantial loss of the polymer's weight average molecular weight, have been developed. The closed cells foams have an open cell content of generally less than 50%, and more preferably an open cell content of less than 20%, and the cells have a maximum diameter of less than 5 mm. The foam may include poly-4-hydroxybutyrate or a copolymer thereof. Preferably, the foam is derived by heating a foam polymer formula to a temperature above the melt temperature of the polymer to form a melt polymer system, adding a blowing agent to produce a foamable melt, extruding the foamable melt through a die to a lower pressure to cause foaming, cooling of the foam, and solidification of the foam. These foam structures can be used for fabrication of medical products.
1. A medical device comprising a foam composition comprising poly-4-hydroxybutyrate (P4HB) homopolymer, wherein the P4HB homopolymer is not crosslinked and wherein the foam comprises closed cells as measured by ASTM D6226-10.
2. The device of claim 1 wherein the device is used for the repair, regeneration or replacement of soft or hard tissue.
3. The device of claim 2 selected from the group consisting of devices to: heal wounds, control bleeding, protect wound beds, prevent infection, apply pressure to a tissue surface or structure, prevent movement of bodily fluids, absorb fluids, deliver bioactive agents, reinforce tissue structures, separate tissues, prevent adhesions, and regenerate tissues.
4. The device of claim 2 selected from the group consisting of: wound dressings, tapes, patches, seals, scaffolds, hemostats, pledgets, wound closure devices, vascular closure devices, repair patches, bulking and filling agents, retention membranes, surgical foams, compression bandages, orthopedic foams, surgical foams, orthodontic devices, drug delivery devices, stents, tissue engineering scaffolds, hernia repair devices, cardiovascular patches, foams for cosmetic surgery, including face lift, neck lift, eyebrow lift, and breast lift, foams for breast reconstruction, slings, rotator cuff repair devices, meniscus repair devices, guided tissue repair/regeneration devices, articular cartilage repair devices, osteochondral repair devices, bone void fillers, nerve guides, tendon repair devices, intracardiac septal defect repair devices, including but not limited to atrial septal defect repair devices and patent foramen ovale closure devices, left atrial appendage closure devices, pericardial patches, vein valves, heart valves, bone marrow scaffolds, meniscus regeneration devices, ligament and tendon grafts, spinal fusion devices, skin substitutes, dural substitutes, and bone graft substitutes.
5. The device of claim 2 further comprising a bioactive agent.
6. A method of using a device of claim 2 , where the device is implanted in the body or applied topically to the surface of the body.
7. A medical device comprising a substantially closed cell foam comprising poly-4-hydroxybutyrate or copolymer thereof that is not crosslinked, wherein the foam is derived by (i) preparing a foam polymer formula comprising poly-4-hydroxybutyrate or copolymer thereof that is not crosslinked, (ii) heating the foam polymer formula to create a polymer melt in an extruder, (iii) introducing a blowing agent to the polymer melt, and (iv) cooling and extruding the foamable melt to form a substantially closed cell foam.
8. The device of claim 1 , wherein the foam has an open cell content of less than 50%.