High strength press quenchable 7XXX alloy
The present invention is directed to a 7xxx series aluminum alloy composition comprising, consisting essentially of, or consisting of (by weight %) of 1.0-1.8% Mg; 7.0-8.3% Zn; 0.10-0.25% Zr; with up to 0.80% Cu and allowable impurities of 0.3% Si, 0.4% Fe, 0.4% Mn, and 0.1% Ti, with other elements restricted as unavoidable impurities limited to 0.05% each and 0.15% total and MgZn 2 range of 7.0-9.9% with the balance being aluminum. This 7xxx series aluminum alloy is capable of being produced to achieve its maximum strength by quenching from an elevated hot working operation, such as extrusion, forging or rolling. In one embodiment the alloy is capable of meeting strength levels in excess of 65 KSI/450 MPa yield tensile strength, 69 KSI/480 MPa ultimate tensile strength and 11% elongation.
1. An extruded, forged or rolled product manufactured from a 7xxx series aluminum alloy having a composition consisting of, (by weight %):
1.0-1.8% Mg
7.3-8.3% Zn
0.10-0.25% Zr
0.02-0.40% Cu
≤0.3% Si
≤<0.4% Fe
≤<0.4% Mn
≤<0.1% Ti
4.0-9.9% MgZn 2
with other elements restricted as unavoidable impurities limited to 0.05% each and 0.15% total; and the balance aluminum, wherein
said extruded, forged or rolled product has a low quench sensitivity as defined as achieving 95% of maximum mechanical properties via forced air quenching.
2. The extruded, forged or rolled product manufactured from claim 1 having a yield tensile strength greater than 450 MPa.
3. The extruded, forged or rolled product manufactured from claim 2 passing SCC testing per ASTM G-44 (Reapproved 2013) stressed to 90% of the product tensile yield strength and exposed for a 60 day test period, with results of pitting only.
4. The extruded, forged or rolled product manufactured from claim 3 having an ultimate tensile strength greater than 480 MPa.
5. An extruded, forged or rolled product manufactured from the alloy of claim 1 passing SCC testing per ASTM G-44 (Reapproved 2013) stressed to 90% of the product tensile yield strength and exposed for a 60 day test period, with results of pitting only.
6. The extruded, forged or rolled product manufactured from claim 5 having an ultimate tensile strength greater than 480 MPa.
7. An extruded, forged or rolled product manufactured from the alloy of claim 1 having an ultimate tensile strength greater than 480 MPa.
8. The extruded, forged or rolled product manufactured from the alloy of claim 1 having a yield tensile strength greater than 450 MPa when exposed to a temperature of 100° C. for 2000 hours.
9. The extruded, forged or rolled product manufactured from the alloy of claim 1 having an ultimate tensile strength greater than 480 MPa when exposed to a temperature of 100° C. for 2000 hours.
10. The extruded, forged or rolled product manufactured from claim 9 having a yield tensile strength greater than 450 MPa when exposed to a temperature of 100° C. for 2000 hours.
11. The extruded, forged or rolled product manufactured from the alloy of claim 1 used in automotive applications.
12. The extruded, forged or rolled product of claim 1 wherein said Cu is 0.02-0.25% Cu.
13. The extruded, forged or rolled product of claim 1 wherein said Zn is a minimum of 0.25% excess Zn.