Blue-emitting nanocrystals with cubic shape and fluoride passivation
This disclosure pertains to the field of nanotechnology. The disclosure provides methods of preparing nanostructures with fluoride passivation. The disclosure also provides methods of preparing nanostructures with fluoride and amine passivation. The nanostructures have high quantum yield, narrow emission peak width, tunable emission wavelength, and colloidal stability. Also provided are nanostructures prepared using the methods. And, nanostructure films and molded articles comprising the nanostructures are also provided.
1. A nanostructure comprising:
a nanocrystal core; and
at least one shell disposed on the core comprising ZnSe, and
at least one shell comprising ZnS and fluoride.
2. The nanostructure of claim 1 , wherein the core comprises ZnSe 1-x Te x , and wherein 0≤x<1.
3. The nanostructure of claim 1 , wherein the fluoride is in the form of a metal fluoride, ammonium fluoride, or tetraalkylammonium fluoride.
4. The nanostructure of claim 1 , wherein the molar ratio of fluoride in the nanostructure to zinc in the nanostructure is between about 0.05 and about 0.35.
5. The nanostructure of claim 1 , wherein the nanostructure exhibits a photoluminescence quantum yield of between about 60% and about 99%.
6. The nanostructure of claim 1 , wherein the core comprises ZnSe and the fluoride is ZnF 2 .
7. The nanostructure of claim 1 , wherein the core comprises ZnSe 1-x Te x and the fluoride is ZnF 2 .
8. A method of preparing the nanostructure of claim 1 , comprising:
(a) providing a nanocrystal core;
(b) admixing the core in (a) with a zinc source and a selenium source to provide a core with a ZnSe shell; and
(c) admixing the core with a ZnSe shell in (b) with a fluoride source; and
(d) infusing a solution comprising a zinc source and a sulfur source into the admixture in (c); to provide the nanostructure.
9. The method of claim 8 , wherein the core comprises ZnSe and the fluoride is ZnF 2 .
10. The method of claim 8 , wherein the core comprises ZnSe 1-x Te x and the fluoride is ZnF 2 .
11. A device comprising the nanostructure of claim 1 .
12. A film comprising the nanostructure of claim 1 and at least one organic resin.
13. A molded article comprising the film of claim 12 .