Polyimide-based composite film and display device comprising same
Embodiments relate to a polyimide-based composite film, which comprises a base film comprising a polyimide-based resin; and a functional layer disposed on the base film, wherein when the side of the functional layer located opposite to the side in contact with the base film is referred to as a first side and when the side of the base film located opposite to the side in contact with the functional layer is referred to as a second side, the adhesiveness index represented by Equation 1 is 3.5 or less.
1. A polyimide-based composite film, which comprises a base film comprising a polyimide-based resin; and a functional layer disposed on the base film,
wherein when the side of the functional layer located opposite to the side in contact with the base film is referred to as a first side and when the side of the base film located opposite to the side in contact with the functional layer is referred to as a second side, the adhesiveness index represented by the following Equation 1 is 3.5 or less:
Adhesiveness
index
=
Fc
×
Ec
Sc
[
Equation
1
]
wherein Sc is (Sz1+Sz2)/2 μm, Fc is (F1+F2)/0.6, Ec is (E1+E2)/40 dyne/cm, Sz1 is the Sz roughness (μm) of the first side, Sz2 is the Sz roughness (μm) of the second side, F1 is the coefficient of static friction between the first side and the second side, F2 is a coefficient of kinetic friction between the first side and the second side, E1 is the surface energy (dyne/cm) of the first side, and the E2 is the surface energy (dyne/cm) of the second side, and
wherein the functional layer comprises an organic resin and an inorganic filler, and the organic resin is at least one selected from the group consisting of an acrylate-based monomer, a urethane acrylate-based oligomer, and an epoxy acrylate-based oligomer.
2. The polyimide-based composite film of claim 1 , wherein the Sz1 is 0.01 μm to 5 μm, and Sz2 is 0.01 μm to 5 μm.
3. The polyimide-based composite film of claim 1 , wherein the Sz1 is 0.01 μm to 4 μm, and Sz2 is 0.01 μm to 4 μm.
4. The polyimide-based composite film of claim 1 , wherein the Sz1 is 0.01 μm to 3 μm, and Sz2 is 0.01 μm to 3 μm.
5. The polyimide-based composite film of claim 1 , wherein the F1 is 0.1 to 0.8, and the F2 is 0.1 to 0.8.
6. The polyimide-based composite film of claim 1 , wherein the E1 is 10 to 100 dyne/cm, and the E2 is 10 to 100 dyne/cm.
7. The polyimide-based composite film of claim 1 , wherein the adhesiveness index is 3 or less.
8. The polyimide-based composite film of claim 1 , wherein the adhesiveness index is 0.01 to 3.
9. The polyimide-based composite film of claim 1 , wherein the base film further comprises a filler.
10. The polyimide-based composite film of claim 9 , wherein the filler is at least one selected from the group consisting of barium sulfate, silica, and calcium carbonate.
11. The polyimide-based composite film of claim 9 , wherein the filler has a particle diameter of 0.01 μm to less than 1.0 μm.
12. The polyimide-based composite film of claim 9 , wherein the base film comprises the filler in an amount of 0.01 to 3% by weight based on the total weight of the base film.
13. The polyimide-based composite film of claim 1 , which has a haze of 3% or less, a yellow index of 5 or less, a tensile modulus of 5 GPa or more, and a transmittance of 80% or more.
14. A display device, which comprises a display panel; and a cover window disposed on the display panel,
wherein the cover window comprises a base film; and a functional layer disposed on the base film, the base film comprises a polyimide-based resin, and when the side of the functional layer located opposite to the side in contact with the base film is referred to as a first side and when the side of the base film located opposite to the side in contact with the functional layer is referred to as a second side, the adhesiveness index represented by the following Equation 1 is 3.5 or less:
Adhesiveness
index
=
Fc
×
Ec
Sc
[
Equation
1
]
wherein Sc is (Sz1+Sz2)/2 μm, Fc is (F1+F2)/0.6, Ec is (E1+E2)/40 dyne/cm, Sz1 is the Sz roughness (μm) of the first side, Sz2 is the Sz roughness (μm) of the second side, F1 is the coefficient of static friction between the first side and the second side, F2 is a coefficient of kinetic friction between the first side and the second side, E1 is the surface energy (dyne/cm) of the first side, and the E2 is the surface energy (dyne/cm) of the second side, and
wherein the functional layer comprises an organic resin and an inorganic filler, and the organic resin is at least one selected from the group consisting of an acrylate-based monomer, a urethane acrylate-based oligomer, and an epoxy acrylate-based oligomer.