Display panel, manufacturing method thereof, and display device
A display panel, a manufacturing method thereof, and a display device. The manufacturing method includes: providing a pretreatment solution containing a water-soluble organic protective agent, and forming, on an anode, a solution layer covering the anode; drying the solution layer to form an adhesive layer; removing the adhesive layer; and drying the anode; where the pretreatment solution contains 10-30% by weight of propylene glycol methyl ether and 70-90% by weight of water.
1. A manufacturing method of a display panel, comprising the following steps:
providing an anode and a pretreatment solution containing a water-soluble organic protective agent, and applying the pretreatment solution onto the anode to form a solution layer covering the anode;
drying the solution layer to form an adhesive layer;
removing the adhesive layer; and
drying the anode;
wherein the pretreatment solution contains 10-30% by weight of propylene glycol methyl ether and 70-90% by weight of water.
2. The manufacturing method of the display panel according to claim 1 , wherein the pretreatment solution has a viscosity of 100-200 cp at 25° C.
3. The manufacturing method of the display panel according to claim 2 , wherein the adhesive layer has a thickness of 0.5-10 μm.
4. The manufacturing method of the display panel according to claim 3 , wherein in the step of drying the solution layer to form an adhesive layer, the drying is performed at a temperature of 35-65° C. for 2-6 min.
5. The manufacturing method of the display panel according to claim 4 , wherein in the step of drying the solution layer to form an adhesive layer, the drying is performed at a temperature of 40-55° C. for 2-5 min.
6. The manufacturing method of the display panel according to claim 4 , wherein in the step of removing the adhesive layer, a water flow at a pressure of 2-7 Pa is used to flush the adhesive layer to remove the adhesive layer; or a solvent is used to remove the adhesive layer.
7. The manufacturing method of the display panel according to claim 6 , wherein in the step of providing an anode and a pretreatment solution containing a water-soluble organic protective agent and applying the pretreatment solution onto the anode to form a solution layer covering the anode, a volume of 2.3-3.5 L of the pretreatment solution is needed to cover per square meter of the anode.
8. The manufacturing method of the display panel according to claim 6 , wherein in the step of drying the anode, the drying is performed at a temperature of 120-230° C. for 30-120 min.
9. The manufacturing method of the display panel according to claim 1 , wherein the forming of the solution layer covering the anode comprises: coating the pretreatment solution onto the anode, by any one of spin coating, ink-jet printing and blade coating, to form the solution layer.
10. The manufacturing method of the display panel according to claim 9 , wherein the pretreatment solution is coated onto the anode, by the spin coating, to form the solution layer, and at least one of a low homogenization speed of 10-150 rpm/10 s and a high homogenization speed of 150-1500 rpm/10 s is used for coating.
11. A display panel, comprising an anode that experienced a pretreatment;
wherein the pretreatment comprises: covering a pretreatment solution onto the anode and drying to form an adhesive layer, removing the adhesive layer and drying the anode; and
the pretreatment solution contains 10-30% by weight of propylene glycol methyl ether and 70-90% by weight of water.
12. The display panel according to claim 11 , wherein the pretreatment solution has a viscosity of 100-200 cp at 25° C.
13. The display panel according to claim 11 , wherein the adhesive layer has a thickness of 0.5-10 μm.
14. The display panel according to claim 11 , wherein the drying to form the adhesive layer is performed at a temperature of 35-65° C. for 2-6 min.
15. The display panel according to claim 14 , wherein the drying to form the adhesive layer is performed at a temperature of 40-55° C. for 2-5 min.
16. The display panel according to claim 11 , wherein the removing the adhesive layer is performed by flushing the adhesive layer using a water flow at a pressure of 2-7 Pa, or is performed by a solvent.
17. The display panel according to claim 11 , wherein a volume of 2.3-3.5 L of the pretreatment solution is needed to cover per square meter of the anode.
18. The display panel according to claim 11 , wherein the drying the anode is performed at a temperature of 120-230° C. for 30-120 min.
19. The display panel according to claim 11 , wherein the pretreatment solution is coated onto the anode, by spin coating, to form a solution layer, wherein at least one of a low homogenization speed of 10-150 rpm/10 s and a high homogenization speed of 150-1500 rpm/10 s is used for coating.
20. A flexible display device, comprising the display panel according to claim 11 .