Water-resistant acrylic coatings
View Patent ↗Water-resistant waterborne acrylic coating materials, systems and methods providing enhanced water resistance and durability are provided. Such coatings extend the service life of roofing systems that are exposed to ponding water and other extreme weather conditions. Coatings described herein exhibit superior water resistance attributes including one or more of water infiltration resistance, wet tensile strength and wet adhesion.
1. A coating material, comprising:
at least one acrylic latex resin;
at least one functional filler;
at least one hydrophobic additive; and
a crosslinking agent;
wherein the acrylic latex resin is selected from the group consisting of hydrophobic resins, self-crosslinking resins, and crosslinkable resins; and
wherein, when the coating material is applied as a 500 micron dry film thickness coating to a roofing substrate, the coating exhibits a water infiltration depth of 120 microns or less after 4 hours at 60° C. and 95% relative humidity.
2. The coating material of claim 1 , wherein the functional filler is selected from the group consisting of silicate minerals, silica, wollastonite, talc, mica, kaolin, feldspar, nepheline syenite, nanoclays, platy fillers, nano-oxide materials, calcium carbonate, aluminum hydroxide, magnesium hydroxide, aluminum tryhydrate, barium sulfate, basalt, zinc oxide, and combinations thereof.
3. The coating material of claim 1 , wherein the hydrophobic additive is selected from the group consisting of hydrophobic copolymer dispersants and salts thereof, nonionic rheology modifiers, PTFE powders, silicone surface additive, high molecular weight polyolefin powder, polyolefin wax and hydrophobic wax dispersions.
4. The coating material of claim 1 , wherein the content of the at least one acrylic latex resin is 20-70 weight percent.
5. The coating material of claim 1 , wherein the content of the at least one functional filler is 25-65 weight percent.
6. The coating material of claim 1 , wherein the content of the at least one hydrophobic additive is 0.5-20 weight percent.
7. The coating material of claim 1 , further comprising a pigment.
8. The coating material of claim 7 , wherein the content of the pigment is 2-15 weight percent.
9. The coating material of claim 1 , wherein the coating has a wet tensile strength of at least 80 psi as measured according to ASTM D882 and/or ASTM D2370.
10. A coating material, comprising:
an acrylic latex resin;
a functional filler;
a hydrophobic additive; and
a crosslinking agent;
wherein the acrylic latex resin is selected from the group consisting of hydrophobic resins, self-crosslinking resins, and crosslinkable resins; and
wherein, when the coating material is applied as a coating to a roofing substrate, the coating has a wet tensile strength of 80 psi to 500 psi as measured according to ASTM D882 and/or ASTM D2370.
11. The coating material of claim 10 , wherein the functional filler is selected from the group consisting of silicate minerals, wollastonite, talc, mica, kaolin, feldspar, nepheline syenite, nanoclays, platy fillers, nano-oxide materials, calcium carbonate, aluminum oxide, magnesium hydroxide, basalt, zinc oxide, and combinations thereof.
12. The coating material of claim 10 , wherein the hydrophobic additive is selected from the group consisting of hydrophobic copolymer dispersants and salts thereof, nonionic rheology modifiers, PTFE powders, and silicone surface additive, high molecular weight polyolefin powder, polyolefin wax hydrophobic wax dispersions.
13. The coating material of claim 10 , wherein the content of the at least one acrylic latex resin is 25-55 weight percent.
14. The coating material of claim 10 , wherein the content of the at least one functional filler is 35-50 weight percent.
15. The coating material of claim 10 , wherein the content of the at least one hydrophobic additive is 1-20 weight percent.
16. The coating material of claim 10 , further comprising a pigment.
17. The coating material of claim 16 , wherein the content of the pigment is 3-15 weight percent.
18. The coating material of claim 10 , wherein the coating exhibits a water infiltration depth of 120 microns or less after 4 hours at 60° C. and 95% relative humidity.
19. The coating material of claim 10 , wherein the coating exhibits a wet tensile strength as measured according to ASTM D882 and/or ASTM D2370 of 80 psi to 500 psi.
20. The coating material of claim 10 , wherein the coating exhibits a wet adhesion strength as measured according to ASTM D903 of 2 pli to 15 pli.
21. A coating material, comprising:
at least one acrylic latex resin;
at least one functional filler having an aspect ratio of 3 to 100;
at least one hydrophobic additive; and
a crosslinking agent;
wherein the acrylic latex resin is selected from the group consisting of hydrophobic resins, self-crosslinking resins, and crosslinkable resins; and
wherein, when the coating material is applied as a 500 micron dry film thickness coating to a roofing substrate, the coating exhibits a greater dry tensile strength than a test coating on a roofing substrate applied with an identical coating material without the at least one functional filler having said aspect ratio.