Particles comprising polyamides with in-backbone optical absorbers and related methods
A method for producing highly spherical polymer particles comprising a polyamide having an optical absorber in a backbone of the polyamide (IBOA-polyamide) may comprise: mixing a mixture comprising the IBOA-polyamide, a carrier fluid that is immiscible with the IBOA-polyamide, and optionally an emulsion stabilizer at a temperature greater than a melting point or softening temperature of the IBOA-polyamide and at a shear rate sufficiently high to disperse the IBOA-polyamide in the carrier fluid; and cooling the mixture to below the melting point or softening temperature of the IBOA-polyamide to form particles comprising the IBOA-polyamide and the emulsion stabilizer, when present, associated with an outer surface of the particles.
1. A composition comprising:
particles comprising a polyamide having an optical absorber in a backbone of the polyamide (IBOA-polyamide) and an emulsion stabilizer comprising nanoparticles associated with an outer surface of the particles, and substantially all of the nanoparticles are associated with the outer surface of the particles,
wherein the particles have a circularity of about 0.90 to about 1.0.
2. The composition of claim 1 , wherein the particles further comprise a thermoplastic polymer that is not the IBOA-polyamide.
3. The composition of claim 1 , wherein the particles further comprise a second polyamide but without an optical absorber in a backbone of the second polyamide.
4. The composition of claim 1 , wherein at least some of the particles have a void.
5. The composition of claim 1 , wherein the nanoparticles are embedded in the outer surface of the particles.
6. The composition of claim 1 , wherein the particles have a D10 of about 0.1 μm to about 125 μm, a D50 of about 0.5 μm to about 200 μm, and a D90 of about 3 μm to about 300 μm, wherein D10<D50<D90.
7. The composition of claim 1 , wherein the particles have a diameter span of about 0.2 to about 10.
8. A method comprising:
depositing the composition of claim 1 optionally in combination with other thermoplastic polymer particles upon a surface in a specified shape; and
once deposited, heating at least a portion of the particles to promote consolidation thereof and form a consolidated body.
9. A composition comprising:
particles comprising a polyamide having an optical absorber in a backbone of the polyamide (IBOA-polyamide) and nanoparticles associated with an outer surface of the particles,
wherein substantially all of the nanoparticles are associated with the outer surface of the particles and the particles have a circularity of about 0.90 to about 1.0, and
wherein the optical absorber comprises at least one optical absorber selected from the group consisting of N,N-di(4-aminophenyl)1-aminopyrene; N,N-bis(4-aminophenyl)-N′-4-methoxyphenyl-N′-4-(1,2,2-triphenylethenyl)phenyl-1,4-phenylenediamine, 4,5-diamino-rhodamine B; rhodamine 123; 2,7-dimethylacridine-3,6-diamine; 2-nitro-1,4-phenylenediamine; 4-[(4-aminophenyl)-(4-iminocyclohexa-2,5-dien-1-ylidene)methyl]aniline hydrochloride; 4,8-diamino-1,5-dihydroxy-9,10-dioxoanthracene-2-sulfonate sodium; calcein; 4-methylumbelliferone-8-methyliminodiacetic acid; 6-carboxyfluorescein; 3,9-perylenedicarboxylic acid; N,N-bis(4-tert-butylphenyl)-N′,N′-bis(4-carboxyphthalimido)-1,4-phenylenediamine; perylene-3,4,9,10-tetracarboxylic dianhydride; alizarin-3-methyliminodiacetic acid; 4-amino-1,8-naphthalimide; and 7-amino-4-methyl-3-coumarinylacetic acid.
10. The composition of claim 1 , wherein the emulsion stabilizer forms a coating that covers at least 25% of the outer surface of the particles.