Protective coating for wood products and method of making same
The present invention is a coating containing approximately 10% glass beads used to protect wood products. Applicant has discovered that the best performance occurs when the concentration of glass beads in the coating ranges from 5 wt % to 10 wt %. A shelf-stable paste is first prepared by combining a solution of modified styrene maleic acid copolymer and a synthetic layered silicate. That paste is then mixed with a binder to form the coating. Preferably, the concentration of glass beads in the paste ranges from 60 wt % to 80 wt %, the concentration of solution of modified styrene maleic acid copolymer ranges from 20 wt % to 25 wt % and the concentration of synthetic layered silicate ranges from 1 wt % to 3 wt %.
1. A process for forming a shelf-stable coating for wood products comprising the steps of:
a) forming a shelf-stable paste, said shelf-stable paste comprising glass beads, a polyether-based dispersant, and synthetic layered silicate; and
b) mixing said shelf-stable paste with a binder to form said shelf-stable coating
wherein the concentration of glass beads in said shelf-stable paste ranges from 60 wt % to 79 wt %, the concentration of polyether-based dispersant in said shelf-stable paste ranges from 20 wt % to 25 wt % and the concentration of synthetic layered silicate in said shelf-stable paste ranges from 1 wt % to 3 wt %.
2. The process of claim 1 , wherein said shelf-stable coating contains between 5 wt % and 15 wt % glass beads.
3. The process of claim 2 , wherein said shelf-stable coating contains 10 wt % glass beads.
4. A process for forming a shelf-stable coating for wood products comprising the steps of:
a) forming a paste pre-mix, said paste pre-mix comprising a polyether-based dispersant and synthetic layered silicate;
b) dispersing glass beads in said paste pre-mix to form a shelf-stable paste; and
c) mixing said shelf-stable paste with a binder to form said shelf-stable coating
wherein the concentration of glass beads in said shelf-stable paste ranges from 60 wt % to 79 wt % the concentration of polyether-based dispersant in said shelf-stable paste ranges from 20 wt % to 25 wt % and the concentration of synthetic layered silicate in said shelf-stable paste ranges from 1 wt % to 3 wt %.
5. The process of claim 4 , wherein said shelf-stable coating contains between 5 wt % and 15 wt % glass beads.
6. The process of claim 5 , wherein said shelf-stable coating contains 10 wt % glass beads.
7. A process for forming a shelf-stable paste for use in a shelf-stable coating for wood products comprising the step of mixing glass beads, a polyether-based dispersant, and synthetic layered silicate to form a shelf-stable paste, wherein the concentration of glass beads in said shelf-stable paste ranges from 60 wt % to 79 wt %, the concentration of polyether-based dispersant in said shelf-stable paste ranges from 20 wt % to 25 wt % and the concentration of synthetic layered silicate in said shelf-stable paste ranges from 1 wt % to 3 wt %.