Method of manufacturing multi-layer electrode for a capacitive pressure sensor and multi-layer electrodes formed therefrom
A multi-layer electrode of a capacitive pressure sensor is manufactured by roll to roll printing a conductive layer onto a polymer layer and forming a mutual capacitance sensor layer of the capacitive pressure sensor, co-extruding a conductive polymer layer and a foam dielectric layer and forming a coextruded layer of the capacitive pressure sensor, and pressure rolling the mutual capacitance sensor layer and the coextruded layer together and forming the multi-layer electrode. The conductive polymer layer includes between about 2 wt. % to about 15 wt. % graphene and between about 0.01 wt. % and 5 wt. % of the carbon nanotubes. Also, the conductive polymer layer has a flexural modulus equal to or greater than 5,000 MPa and an electrical resistivity less than or equal to 10 Ohm/mm 3 , and the polymer layer and/or the conductive polymer layer is formed from recycled polyethylene terephthalate.
1. A multi-layer electrode of a capacitive pressure sensor manufactured according to a method comprising:
roll to roll printing a conductive layer onto a polymer layer and forming an XY layer of the capacitive pressure sensor;
co-extruding a conductive polymer layer and a foam dielectric layer and forming coextruded layers of the capacitive pressure sensor; and
pressure rolling the XY layer and the coextruded layers together and forming the multi-layer electrode.
2. The multi-layer electrode according to claim 1 , wherein the roll to roll printing comprises rotogravure printing conductive ink onto the polymer layer and forming the conductive layer.
3. The multi-layer electrode according to claim 2 , wherein the conductive ink layer has a thickness between about 10 μm to about 100 μm.
4. The multi-layer electrode according to claim 2 , wherein the conductive ink layer comprises at least one or silver, graphene, carbon, and indium tin oxide.
5. The multi-layer electrode according to claim 1 , wherein the conductive polymer layer comprises polyethylene terephthalate (PET).
6. The multi-layer electrode according to claim 5 , wherein the PET is recycled PET.
7. The multi-layer electrode according to claim 1 , wherein the conductive polymer layer comprises a filler.
8. The multi-layer electrode according to claim 7 , wherein the filler comprises graphene and carbon nanostructures.
9. The multi-layer electrode according to claim 8 , wherein the carbon nanostructures comprise carbon nanotubes.
10. The multi-layer electrode according to claim 9 , wherein the conductive polymer layer comprises between about 2 wt. % to about 15 wt. % of the graphene and between about 0.01 wt. % and 5 wt. % of the carbon nanotubes.
11. The multi-layer electrode according to claim 10 , wherein the conductive polymer layer has a flexural modulus equal to or greater than 5,000 MPa.
12. The multi-layer electrode according to claim 10 , wherein the conductive polymer layer has an electrical resistivity less than or equal to 10 Ohm/mm 3 .
13. The multi-layer electrode according to claim 10 , wherein the conductive polymer layer has a flexural modulus equal to or greater than 5,000 MPa and an electrical resistivity less than or equal to 10 Ohm/mm 3 .
14. The multi-layer electrode according to claim 1 , wherein the conductive polymer layer comprises between about 2 wt. % to about 15 wt. % of graphene, between about 0.01 wt. % and 5 wt. % of carbon nanotubes, a flexural modulus equal to or greater than 5,000 MPa and an electrical resistivity less than or equal to 10 Ohm/mm 3 .
15. The multi-layer electrode according to claim 14 , wherein the conductive polymer layer comprises between about 8 wt. % to about 10 wt. % of the graphene and between about 0.01 wt. % and 1 wt. % of the carbon nanotubes.
16. A multi-layer electrode for a capacitive pressure sensor manufactured according to a method comprising:
roll to roll rotogravure printing a conductive ink layer onto a polymer layer and forming an XY layer of the multi-layer electrode;
co-extruding a conductive polymer layer with a foam dielectric layer and forming coextruded layers of the multi-layer electrode; and
pressure rolling the XY layer and the coextruded layers together and forming the multi-layer electrode, wherein the dielectric foam layer is in contact with the conductive ink layer.
17. The multi-layer electrode according to claim 16 , wherein the conductive polymer layer comprises between about 2 wt. % to about 15 wt. % of graphene, between about 0.01 wt. % and 5 wt. % of carbon nanotubes.
18. The multi-layer electrode according to claim 17 , wherein the conductive polymer layer has a flexural modulus equal to or greater than 5,000 MPa and an electrical resistivity less than or equal to 10 Ohm/mm 3 .
19. A multi-layer electrode for a capacitive pressure sensor manufactured according to a method comprising:
roll to roll rotogravure printing a conductive ink layer onto a polymer layer and forming an XY layer of the multi-layer electrode;
co-extruding a conductive polymer layer with a foam dielectric layer and forming coextruded layers of the multi-layer electrode, wherein the polymer layer comprises between about 2 wt. % to about 15 wt. % of graphene, between about 0.01 wt. % and 5 wt. % of carbon nanotubes; and
pressure rolling the XY layer and the coextruded layers together and forming the multi-layer electrode, wherein the dielectric foam layer is in contact with the conductive ink layer.
20. The multi-layer electrode according to claim 19 , wherein the conductive polymer layer has a flexural modulus equal to or greater than 5,000 MPa and an electrical resistivity less than or equal to 10 Ohm/mm 3 .