Thrust roller bearing
A thrust roller bearing includes a plurality of radially arranged rollers, and a pair of annular washers having raceway surfaces on which the rollers roll, the raceway surfaces being arranged to face each other. The roller is made of high-carbon chromium bearing steel, and contains 1.1 mass % to 1.6 mass % of carbon and 0.1 mass % to 0.6 mass % of nitrogen in a range of 0.1 mm from a surface. A surface compressive residual stress is smaller than −900 MPa, a surface roughness is 0.01 to 0.10 in terms of Rvk and 0.01 to 0.08 in terms of Rk, and a Vickers hardness of the surface is 860 to 980. At least one of the washers is made of carbon steel, and surface roughnesses of the raceway surfaces are 0.05 to 0.20 in terms of Rvk and 0.08 to 0.15 in terms of Rk.
1. A thrust roller bearing, comprising:
a plurality of rollers; and
a pair of annular washers having raceway surfaces on which the rollers roll, the raceway surfaces being arranged to face each other, wherein:
the roller is made of high-carbon chromium bearing steel, and contains 1.1 mass % to 1.6 mass % of carbon and 0.1 mass % to 0.6 mass % of nitrogen in a range of 0.1 mm from a surface;
an absolute value of a surface compressive residual stress is greater than 900 MPa, a surface roughness is 0.01 to 0.10 in terms of Rvk and 0.01 to 0.08 in terms of Rk, and a Vickers hardness of the surface is 860 to 980; and
at least one of the washers is made of carbon steel, and surface roughnesses of the raceway surfaces are 0.05 to 0.20 in terms of Rvk and 0.08 to 0.15 in terms of Rk.
2. The thrust roller bearing according to claim 1 , wherein both of the washers are made of carbon steel, and the surface roughnesses of the raceway surfaces are 0.05 to 0.20 in terms of Rvk and 0.08 to 0.15 in terms of Rk.