Magnesium alloy sheet and method for producing same

1. A magnesium alloy sheet comprising:

0.5 to 3.5 wt % of Al, 0.5 to 1.5 wt % of Zn, 0.1 to 1.0 wt % of Ca, 0.01 to 1.0 wt % of Mn, a remainder of Mg, and other inevitable impurities with respect to an entire 100 wt % of the magnesium alloy sheet,

wherein an average crystal grain size of the magnesium alloy sheet is 3 to 15 μm,

wherein the magnesium alloy sheet has a limited bending radius (LBR) value in a rolling direction (RD) at equal to or greater than 150° C. that is equal to or less than 0.5,

wherein an absolute value of a difference between the limited bending radius (LBR) value in the rolling direction (RD) and transverse direction (TD) at equal to or greater than 150° C. is 0.4 to 1.4.

2. The magnesium alloy sheet of claim 1 , wherein

the magnesium alloy sheet includes a stringer, and

a length of the stringer in the rolling direction (RD) is equal to or less than a maximum value of 50 μm.

3. The magnesium alloy sheet of claim 2 , wherein

a thickness of the stringer in the transverse direction (TD) is equal to or less than a maximum value of 1 μm on the magnesium alloy sheet.

4. The magnesium alloy sheet of claim 1 , wherein

the magnesium alloy sheet has the limited bending radius (LBR) value in the transverse direction (TD) at equal to or greater than 150° C. that is equal to or less than 1.5.

5. The magnesium alloy sheet of claim 1 , wherein a thickness of the magnesium alloy sheet is 0.8 to 1.7 mm.