Lithium ion battery using crosslinkable separator

1. A separator for an electricity storage device comprising a silane-modified polyolefin, wherein a silane crosslinking reaction of the silane-modified polyolefin is initiated when the separator for an electricity storage device contacts with an electrolyte solution.

2. The separator for an electricity storage device according to claim 1 , wherein the silane-modified polyolefin is not a master batch resin containing a dehydrating condensation catalyst that crosslinks the silane-modified polyolefin.

3. The separator for an electricity storage device according to claim 1 , wherein the separator for an electricity storage device comprises polyethylene in addition to the silane-modified polyolefin.

4. The separator for an electricity storage device according to claim 3 , wherein the weight ratio of the silane-modified polyolefin and the polyethylene (silane-modified polyolefin weight/polyethylene weight) is 0.05/0.95 to 0.40/0.60.

5. A separator for an electricity storage device comprising a silane-modified polyolefin, wherein silane crosslinking reaction of the silane-modified polyolefin takes place when the separator for an electricity storage device contacts with an electrolyte solution.

6. An electricity storage device comprising an electrode, the separator for an electricity storage device according to claim 1 , and a nonaqueous electrolyte solution.

7. A method for producing the separator for an electricity storage device according to claim 1 , wherein the method comprises the following steps:

(1) a sheet-forming step in which a mixture of a silane-modified polyolefin, polyethylene and a plasticizer is extruded, cooled to solidification and cast into a sheet to obtain a sheet;

(2) a stretching step in which the sheet is stretched at least in a uniaxial direction to obtain a stretched sheet;

(3) a porous body-forming step in which the plasticizer is extracted from the stretched sheet in the presence of an extraction solvent, forming pores in the stretched sheet to form a porous body; and

(4) a heat treatment step in which the porous body is subjected to heat treatment.

8. An electricity storage device assembly kit comprising the following two elements:

(1) an exterior body housing a laminated stack or wound body of electrodes and the separator for an electricity storage device according to claim 1 ; and

(2) a container housing a nonaqueous electrolyte solution.

9. The electricity storage device assembly kit according to claim 8 , wherein the nonaqueous electrolyte solution includes a fluorine (F)-containing lithium salt.

10. The electricity storage device assembly kit according to claim 8 , wherein the nonaqueous electrolyte solution includes lithium hexafluorophosphate (LiPF 6 ).

11. The electricity storage device assembly kit according to claim 8 , wherein the nonaqueous electrolyte solution is an acid solution and/or a base solution.

12. A method for producing an electricity storage device comprising the following steps:

a step of preparing the electricity storage device assembly kit according to claim 8 , and

a step of contacting the separator for an electricity storage device in element (1) of the electricity storage device assembly kit with the nonaqueous electrolyte solution in element (2), to initiate silane crosslinking reaction of the silane-modified polyolefin.

13. The method for producing an electricity storage device according to claim 12 , which further comprises the following steps:

a step of connecting lead terminals to the electrodes of element (1), and

a step of carrying out at least one cycle of charge-discharge.

14. An electricity storage device comprising an electrode, the separator for an electricity storage device according to claim 5 , and a nonaqueous electrolyte solution.

15. A method for producing the separator for an electricity storage device according to claim 5 , wherein the method comprises the following steps:

(1) a sheet-forming step in which a mixture of a silane-modified polyolefin, polyethylene and a plasticizer is extruded, cooled to solidification and cast into a sheet to obtain a sheet;

(2) a stretching step in which the sheet is stretched at least in a uniaxial direction to obtain a stretched sheet;

(3) a porous body-forming step in which the plasticizer is extracted from the stretched sheet in the presence of an extraction solvent, forming pores in the stretched sheet to form a porous body; and

(4) a heat treatment step in which the porous body is subjected to heat treatment.

16. An electricity storage device assembly kit comprising the following two elements:

(1) an exterior body housing a laminated stack or wound body of electrodes and the separator for an electricity storage device according to claim 5 ; and

(2) a container housing a nonaqueous electrolyte solution.

17. The electricity storage device assembly kit according to claim 16 , wherein the nonaqueous electrolyte solution includes a fluorine (F)-containing lithium salt.

18. The electricity storage device assembly kit according to claim 16 , wherein the nonaqueous electrolyte solution includes lithium hexafluorophosphate (LiPF 6 ).

19. The electricity storage device assembly kit according to claim 16 , wherein the nonaqueous electrolyte solution is an acid solution and/or a base solution.

20. A method for producing an electricity storage device comprising the following steps:

a step of preparing the electricity storage device assembly kit according to claim 16 , and

a step of contacting the separator for an electricity storage device in element (1) of the electricity storage device assembly kit with the nonaqueous electrolyte solution in element (2), to initiate silane crosslinking reaction of the silane-modified polyolefin.

21. The method for producing an electricity storage device according to claim 20 , which further comprises the following steps:

a step of connecting lead terminals to the electrodes of element (1), and

a step of carrying out at least one cycle of charge-discharge.

22. A method for producing a separator for an electricity storage device, which comprises the following steps:

(1) a sheet-forming step in which a silane-modified polyolefin, polyethylene and a plasticizer are extruded into a sheet using an extruder, cooled to solidification and shaped into a molded sheet;

(2) a stretching step in which the molded sheet is subjected to biaxial stretching to a 20-fold to 250-fold area increase to form a stretched sheet;

(3) a porous body-forming step in which the plasticizer is extracted from the stretched sheet to form a porous body;

(4) a heat treatment step in which the porous body is subjected to heat treatment and subjected to stretching and relaxation in the transverse direction to obtain a heat-treated porous body;

(8B) a coating step in which an inorganic porous layer including inorganic particles and a resin binder is formed on at least one surface of the heat-treated porous body to form a silane-crosslinking precursor; and

(9) an assembly step in which a laminated stack or wound body of electrodes and the silane-crosslinking precursor, and a nonaqueous electrolyte solution, are housed in an exterior body, contacting the silane-crosslinking precursor with the nonaqueous electrolyte solution.