METAL SURFACE TREATMENT COMPOSITION HAVING EXCELLENT SLIP RESISTANCE, AND METAL MATERIAL TO WHICH SAME IS APPLIED
The present invention relates to a chromium-free metal surface treatment composition comprising 10-30 parts by weight of a silane-based compound, 0.5-6 parts by weight of an organic acid, 0.1-3 parts by weight of a vanadium compound, 0.1-3 parts by weight of a magnesium compound, 0.5-3 parts by weight of a wax and a balance of a solvent. The metal surface treatment composition of the present invention can ensure slip resistance and required properties such as corrosion resistance and workability, thereby enabling a metal material to be prevented from slipping or falling off during processing, pipe making and the like.
1 . A chromium-free metal surface treatment composition, comprising:
10-30 parts by weight of a silane-based compound, 0.5-6 parts by weight of an organic acid, 0.1-3 parts by weight of a vanadium compound, 0.1-3 parts by weight of a magnesium compound, 0.5-3 parts by weight of a wax and a balance of a solvent.
2 . The chromium-free metal surface treatment composition of claim 1 , wherein a wax is a polypropylene wax.
3 . The chromium-free metal surface treatment composition of claim 1 , wherein a weight average molecular weight of a wax is 2,000-10,000.
4 . The chromium-free metal surface treatment composition of claim 1 , wherein a melting point of a wax is 130-160° C.
5 . The chromium-free metal surface treatment composition of claim 1 , wherein an organic acid is one or more selected from among formic acid, phosphoric acid, and acetic acid.
6 . The chromium-free metal surface treatment composition of claim 1 , wherein a silane-based compound is one or more selected from a group consisting of epoxy-based silane and amino-based silane.
7 . The chromium-free metal surface treatment composition of claim 6 , wherein epoxy-based silane is one or more selected from among vinylmethoxy silane, vinyltrimethoxy silane, vinylepoxy silane, vinyltriepoxy silane, 3-aminopropyltriepoxy silane, 3-glycidoxy propyltrimethoxy silane, 3-methacryloxypropyltrimethoxy silane, 3-mercaptopropyl trimethoxy silane, N-(1,3-dimethylbutylidene)-3-(triepoxy silane)-1-propanamine, and N,N-bis[3-(trimethoxysilyl) propyl] ethylenediamine.
8 . The chromium-free metal surface treatment composition of claim 6 , wherein amino-based silane is one or more selected from among N-(β-aminoethyl)-γ-amino propylmethyldimethoxysilane, N-(β-aminoethyl)-γ-aminopropyltrimethoxysilane, γ-glycidoxypropyltriethoxysilane, γ-glycine cydoxitrimethyldimethoxysilane, 2-(3,4-epoxycyclohexyl)ethyltrimethoxysilane, γ-methacryloxypropyltrimethoxysilane, γ-methacryloxypropyltriethoxysilane, γ-mercaptopropyltrimethoxysilane, γ-mercapto propyltriethoxysilane, 3-amino propyl triethoxy silane, and N-[2-(vinylbenzylamino)ethyl]-3-aminopropyltrimethoxysilane.
9 . The chromium-free metal surface treatment composition of claim 1 , further comprising:
0.01-1 parts by weight of a defoamer and 1-2 parts by weight of a wetting agent.
10 . The chromium-free metal surface treatment composition of claim 9 , wherein a defoamer is n-methylethanol amine.
11 . The chromium-free metal surface treatment composition of claim 9 , wherein the wetting agent is one or more selected from among isopropyl alcohol, 2-ethyl-1-hexanol, 2-butoxyethanol, dipropylene glycol, ethylene glycol, n-propyl alcohol, and propylene glycol.
12 . A chromium-free surface treatment metal material having excellent slip resistance, comprising:
a metal material; and
a coating layer formed on the metal material, and formed as a cured product of a metal surface treatment composition including 10-30 parts by weight of a silane-based compound, 0.5-6 parts by weight of an organic acid, 0.1-3 parts by weight of a vanadium compound, 0.1-3 parts by weight of a magnesium compound, 0.5-3 parts by weight of a wax and a balance of a solvent.
13 . The chromium-free surface treatment metal material of claim 12 , wherein a thickness of the coating layer is 0.5-10 μm.
14 . The chromium-free surface treatment metal material of claim 12 , wherein a coefficient of friction of the coating layer is 0.4-0.6.
15 . The chromium-free surface treatment metal material of claim 12 , wherein a wax is a polypropylene wax.
16 . The chromium-free surface treatment metal material of claim 12 , wherein a weight average molecular weight of a wax is 2,000-10,000.
17 . The chromium-free surface treatment metal material of claim 12 , wherein a melting point of a wax is 130-160° C.
18 . The chromium-free surface treatment metal material of claim 12 , wherein the metal surface treatment composition further includes 0.01-1 parts by weight of a defoamer and 1-2 parts by weight of a wetting agent.
19 . The chromium-free surface treatment metal material of claim 12 , wherein the metal material is one selected from among a stainless steel sheet, a galvanized steel sheet, an aluminum plated steel sheet, and an alloy plated steel sheet.