Electrical steel sheet adhesive coating composition, electrical steel sheet product, and manufacturing method therefor
An electrical steel sheet adhesive coating composition according to an exemplary embodiment of the present invention includes, based on 100 wt % of the total solids: a resin at 20 to 40 wt % and having an average particle diameter of 10 to 300 nm; an inorganic nanoparticle at 10 to 35 wt % bonded with the resin; a metal phosphoric acid salt at 10 to 30 wt %; and phosphoric acid at 10 to 40 wt %. An electrical steel sheet product according to an exemplary embodiment of the present invention includes a plurality of electrical steel sheets; and an adhesive layer disposed between the plurality of electrical steel sheets, wherein the adhesive layer includes a metal of one or more kinds among Al, Mg, Ca, Co, Zn, Zr, and Fe at 0.5 to 30 wt %, N at 0.1 to 10 wt %, C at 0.1 to 5 wt %, P at 1 to 30 wt %, a metal of one or more kinds among Si and Ti at 10 to 30 wt %, and a balance of O.
1. An electrical steel sheet product comprising:
a plurality of electrical steel sheets; and
an adhesive layer disposed between the plurality of electrical steel sheets,
wherein the adhesive layer includes:
a first metal at 0.5 to 30 wt %, the first metal is at least one element selected from the group consisting of Al, Mg, Ca, Co, Zn, Zr, and Fe;
N at 0.1 to 10 wt %;
C at 0.1 to 5 wt %;
P at 1 to 30 wt %;
a second metal at 10 to 30 wt %, the second metal is at least one element selected from the group consisting of Si and Ti; and
a balance of O, and
in the adhesive layer, for a cross-sectional area of the adhesive layer, a fraction of an area occupied by pores is 10 to 70% and an average diameter of the pores is 20% or less of an adhesive layer thickness.
2. The electrical steel sheet product of claim 1 , wherein
the first metal is Al.
3. The electrical steel sheet product of claim 1 , wherein
the second metal is Si.
4. The electrical steel sheet product of claim 1 , wherein
the thickness of the adhesive layer is 0.5 to 40 μm.
5. The electrical steel sheet product of claim 1 , further comprising
an oxidation layer disposed between the electrical steel sheet and the adhesive layer.
6. The electrical steel sheet product of claim 5 , wherein the oxidation layer includes:
a third metal at 1 to 20 wt %, the third metal is at least one element selected from the group consisting of Al, Mg, Ca, Co, Zn, Zr, and Fe;
N at 0.1 to 10 wt %;
C at 0.1 wt % or less;
P at 10 to 40 wt %;
a fourth metal at 5 to 30 wt %, the fourth metal is at least one element selected from the group consisting of Si and Ti; and
a balance of O.
7. The electrical steel sheet product of claim 5 , wherein
in the oxidation layer, for the cross-sectional area of the oxidation layer, a fraction of an area occupied with the pores is 10% or less.
8. The electrical steel sheet product of claim 5 , wherein
the thickness of the oxidation layer is 10 to 500 nm.
9. The electrical steel sheet product of claim 5 , wherein
the average diameter of the pores is 20% or less of the oxidation layer thickness.