Thermal insulating glass, method for preparing the same and thermal insulating glass product
A thermal insulating glass includes a glass substrate and a thermal insulating layer. The thermal insulating layer includes composite tungsten oxide and a binder. The composite tungsten oxide is represented by formula (1): M x WO 3-y A y (1), where M is an alkali metal element or an alkaline earth metal element, W is tungsten, O is oxygen, A is a halogen element, and 0<x≤1 and 0≤y≤0.5. And the binder includes one or more of the following components: silicon dioxide, titanium dioxide, and aluminium oxide. The thermal insulating glass can prevent the occurrence of obscuration. The thermal insulating has infrared reflectivity, high strength and good wear resistance, and can effectively resist high temperature and strong oxidation environment.
1. A thermal insulating glass comprising:
a glass substrate; and
a thermal insulating layer;
wherein the thermal insulating layer comprises composite tungsten oxide and a binder, and wherein the composite tungsten oxide is represented by formula (1):
M x WO 3-y A y (1),
and wherein M is an alkali metal element or an alkaline earth metal element, W is tungsten, O is oxygen, A is a halogen element, and 0<x≤1 and 0≤y≤0.5,
and wherein the binder comprises one or more of the following components: silicon dioxide, titanium dioxide, and aluminium oxide.
2. The thermal insulating glass according to claim 1 , wherein y=0.
3. The thermal insulating glass according to claim 1 , wherein M is cesium.
4. The thermal insulating glass according to claim 1 , wherein the thickness of the thermal insulating layer is from 50 nm to 50 μm.
5. The thermal insulating glass according to claim 4 , wherein the thickness of the thermal insulating layer is from 500 nm to 5 μm.
6. The thermal insulating glass according to claim 1 , wherein the weight ratio of the binder to the composite tungsten oxide in the thermal insulating layer is from 1:1 to 1:1000.
7. The thermal insulating glass according to claim 1 , wherein the thermal insulating glass further comprises a barrier layer positioned between the glass substrate and the thermal insulating layer.
8. The thermal insulating glass according to claim 7 , wherein the barrier layer comprises one or more of the following components: silicon dioxide, titanium dioxide, and aluminium oxide.
9. The thermal insulating glass according to claim 8 , wherein the purity of components silicon dioxide, titanium dioxide, and aluminium oxide is equal to or greater than 99%.
10. The thermal insulating glass according to claim 7 , wherein the dense degree of the barrier layer is equal to or greater than 90%.
11. The thermal insulating glass according to claim 7 , wherein the thickness of the barrier layer is from 5 nm to 500 nm.
12. The thermal insulating glass according to claim 1 , wherein the thermal insulating glass further comprises a protective powder layer positioned on the thermal insulating layer and the protective powder layer comprises one or more of the following components: carbon powder, iron powder, zinc powder, aluminum powder, and reducing salt.
13. The thermal insulating glass according to claim 12 , wherein the thermal insulating glass further comprises a protective glass positioned on the protective powder layer.
14. A thermal insulating glass product comprising the thermal insulating glass according to claim 1 .
15. A method for preparing the thermal insulating glass according to claim 1 , comprising:
(a) providing a glass substrate;
(a1) optionally, providing a barrier layer on the glass substrate;
(b) providing a thermal insulating layer on the glass substrate or on the barrier layer;
(c) optionally, providing a protective powder layer on the thermal insulating layer;
(d) optionally, providing a protective glass on the protective powder layer.