(Meth)acrylic polymer composition comprising particles, its method of preparation and its use as masterbatch

1. A polymeric masterbatch composition MB1 comprising:

a) a carrier material comprising a (meth)acrylic polymer AP1 comprising at least 50 wt % acrylic and/or methacrylic monomers in its polymeric chain, and

b) a polymeric silicone particle PP1 having a weight average particle diameter between 1 μm and 10 μm,

wherein the particle PP1 comprises between 0.5 wt % and 50 wt % of the composition based on a total weight of the components a) and b);

wherein the polymeric masterbatch composition MB1 further comprises:

c) a polymeric (meth)acrylic particle PP2 having a weight average particle diameter between 20 μm and 100 μm, wherein the polymeric (meth)acrylic particle PP2 represents between 10 wt % and 49 wt % of the composition based on a total weight of the components a), b) and c);

wherein the polymeric silicone particle PP1 and the polymeric (meth)acrylic particle PP2 are dispersed in the carrier material, and

wherein a difference of refraction index between the polymeric (meth)acrylic particle PP2 and the (meth)acrylic polymer AP1 is at least 0.005.

2. The polymeric masterbatch composition MB1 according to claim 1 , wherein the polymeric silicone particle PP1 has a refractive index between 1.30 and 1.45.

3. The polymeric masterbatch composition MB1 according to claim 1 , wherein the polymeric silicone particle PP1 has a weight average particle diameter between 1 μm and 9 μm.

4. The polymeric masterbatch composition MB1 according to claim 1 , wherein at least 50 wt % of monomer units in polymer chains of the polymeric particle PP2 comprise acrylic and/or methacrylic monomers.

5. The polymeric masterbatch composition MB1 according to claim 1 , wherein the polymeric (meth)acrylic particle PP2 has a weight average particle diameter between 35 μm and 90 μm.

6. The polymeric masterbatch composition MB1 according to claim 1 , wherein the (meth)acrylic polymer AP1 is a homo- or copolymer of methyl methacrylate (MMA) and wherein at least 50 wt % of monomer units in polymer chains of the homo- or copolymer of MMA comprise methyl methacrylate.

7. The polymeric masterbatch composition MB1 according to claim 1 , wherein the weight average particle diameter of the polymeric (meth)acrylic particle PP2 is at least three times greater than the weight average particle diameter of the silicone particles PP1.

8. The polymeric masterbatch composition MB1 according to claim 1 , wherein the weight average particle diameter of the polymeric (meth)acrylic particle PP2 is at most one hundred times greater than the weight average particle diameter of silicone particles PP1.

9. The polymeric masterbatch composition MB1 according to claim 1 , wherein a difference of refraction index between the (meth)acrylic polymer AP1 and the silicone particles PP1 is at least 0.01.

10. A process for the preparation of a polymeric masterbatch composition MB1 according to claim 1 , wherein said process comprises the step of blending the components a), b) and c).

11. The process according to claim 10 , wherein the blending is accomplished by compounding.

12. A process for the preparation of a polymeric composition PC1 comprising the step of blending the masterbatch composition MB1 according to claim 1 at least one time with additional (meth)acrylic polymer AP1, wherein the polymeric composition PC1 comprises:

a) the (meth)acrylic polymer AP1 of the masterbatch composition MB1 and the additional (meth)acrylic polymer AP1;

b) the polymeric silicone particle PP1 having a weight average particle diameter between 1 μm and 10 μm;

c) the polymeric (meth)acrylic particle PP2 having a weight average particle diameter between 20 μm and 100 μm,

wherein the polymeric silicone particle PP1 comprises between 0.05 and 10 wt % of the polymeric composition PC1.

13. The process for the preparation of a polymeric composition PC1 according to claim 12 , wherein the particle PP2 comprises between 0.1 wt % and 20 wt % of the polymeric composition PC1.