Multi-dimensional hemostatic product and method for producing the same

1. A printed hemostatic product having three-dimensions and being made of a stack of layers deposited on one another from a first external layer up to a second external layer, wherein a plurality of adjacent layers of the stack of layers are joined together, and wherein each of the plurality of adjacent layers of the stack of layers has at least one portion made from an hemostatic flowable with a composition comprising:

non-cross-linked collagen of the fibrillar type comprising a content of fibrous collagen and/or fibrillar collagen of at least 70% by weight relative to the total weight of the collagen; and

at least one monosaccharide

wherein at least one layer of the plurality of adjacent layers of the stack of layers has several portions made from hemostatic flowables with different compositions.

2. The printed hemostatic product of claim 1 , wherein at least one layer of the plurality of adjacent layers of the stack of layers is fully made from the same hemostatic flowable.

3. The printed hemostatic product of claim 1 , wherein at least one of the first and second external layers of the stack of layers has a portion made from the hemostatic flowable.

4. The printed hemostatic product of claim 3 , wherein the at least one of the first and second external layers is fully made from the same hemostatic flowable.

5. The printed hemostatic product of claim 1 , wherein at least one layer of the stack of layers comprises a portion made from an hemostatic flowable having swelling properties different from the swelling properties of the other layers of the stack of layers.

6. The printed hemostatic product of claim 1 , wherein the hemostatic flowable is made with an hemostatic powder having a composition comprising:

collagen of the fibrillar type comprising a content of fibrous collagen and/or fibrillar collagen of at least 70% by weight relative to the total weight of the collagen, said collagen being in an amount ranging from 75% to 96% by weight relative to the total weight of the composition of the hemostatic powder, and

least one monosaccharide in an amount ranging from 1% to 12.5% by weight relative to the total weight of the composition of the hemostatic powder.

7. A method of producing a printed hemostatic product of claim 1 , with an hemostatic flowable as a printing ink for a three-dimensional printer, wherein the hemostatic flowable is made of a hemostatic powder mixed with a saline solution, wherein the hemostatic powder has a composition comprising:

non-cross-linked collagen of the fibrillar type comprising a content of fibrous collagen and/or fibrillar collagen of at least 70% by weight relative to the total weight of the collagen; and

at least one monosaccharide.

8. The method of claim 7 , wherein the composition of the hemostatic powder forming the hemostatic flowable comprises:

collagen of the fibrillar type comprising a content of fibrous collagen and/or fibrillar collagen of at least 70% by weight relative to the total weight of the collagen, said collagen being in an amount ranging from 75% to 96% by weight relative to the total weight of the composition of the hemostatic powder; and

east one monosaccharide in an amount ranging from 1% to 12.5% by weight relative to the total weight of the composition of the hemostatic powder.

9. Method of manufacturing an hemostatic product of claim 1 having three dimensions with a three-dimensional additive printer, comprising the following steps:

a) providing a three-dimensional model to the three-dimensional additive printer, said three-dimensional model corresponding to the structure of the hemostatic product to be manufactured, and processing said three-dimensional model to define a printing pattern with a plurality of layers designed to be stacked on one another so as to form a stack of layers corresponding to the three-dimensional model;

b) providing at least one hemostatic flowable to the three-dimensional additive printer for use as a printing ink, wherein said flowable is made of an hemostatic powder mixed with a saline solution, wherein the hemostatic powder has a composition comprising:

non-cross-linked collagen of the fibrillar type comprising a content of fibrous collagen and/or fibrillar collagen of at least 70% by weight relative to the total weight of the collagen; and

at least one monosaccharide;

c) printing the hemostatic product with the three-dimensional additive printer by depositing printing ink to successively print layers on one another, said forming comprising depositing the hemostatic flowable with the three-dimensional additive printer to form at least one portion of at least one layer of the stack of layers.

10. The method of claim 9 , wherein at least one layer of the stack of layers is entirely made with the deposition of the hemostatic flowable.

11. The method of claim 9 , wherein in step b), a plurality of hemostatic flowables are provided to the three-dimensional additive printer for use as printing inks, said hemostatic flowables having different compositions.

12. The method of claim 9 , wherein the composition of the hemostatic powder forming the hemostatic flowable comprises:

collagen of the fibrillar type comprising a content of fibrous collagen and/or fibrillar collagen of at least 70% by weight relative to the total weight of the collagen, said collagen being in an amount ranging from 75% to 96% by weight relative to the total weight of the composition of the hemostatic powder; and

least one monosaccharide in an amount ranging from 1% to 12.5% by weight relative to the total weight of the composition of the hemostatic powder.

13. The method of claim 9 , wherein the printing step c) is done at ambient atmosphere.

14. The method of claim 9 , wherein after the hemostatic product has been formed in the printing step c), a coating step d) is performed wherein a solution including a coagulation factor is used to coat an external surface of the hemostatic product.

15. The method of claim 14 , wherein the coating step d) is performed by spraying the solution including a coagulation factor on the external surface of the hemostatic product.

16. The method of claim 9 , wherein after the hemostatic product has been formed in the printing step c), a soaking step e) is performed wherein the hemostatic product is soaked in a solution including a coagulation factor.

17. The method of claim 9 , wherein the final step of manufacturing the hemostatic product consists in maintaining the printed hemostatic product in ambient atmosphere for a predetermined resting period.

18. The method of claim 9 , wherein the whole process is performed at ambient atmosphere without any photo-stimulation or heat stimulation of the hemostatic product.

19. A printed hemostatic product having three-dimensions and being made of a stack of layers deposited on one another from a first external layer up to a second external layer, wherein a plurality of adjacent layers of the stack of layers are joined together, and wherein each of the plurality of adjacent layers of the stack of layers has at least one portion made from an hemostatic flowable with a composition comprising:

non-cross-linked collagen of the fibrillar type comprising a content of fibrous collagen and/or fibrillar collagen of at least 70% by weight relative to the total weight of the collagen; and

at least one monosaccharide;

wherein all layers of the stack of layers have the same composition.

20. A printed hemostatic product having three-dimensions and being made of a stack of layers deposited on one another from a first external layer up to a second external layer, wherein a plurality of adjacent layers of the stack of layers are joined together, and wherein each of the plurality of adjacent layers of the stack of layers has at least one portion made from an hemostatic flowable with a composition comprising:

non-cross-linked collagen of the fibrillar type comprising a content of fibrous collagen and/or fibrillar collagen of at least 70% by weight relative to the total weight of the collagen; and

at least one monosaccharide;

wherein the first and second external layers of the stack of layers are made from an hemostatic flowable of the same composition, and wherein each layer of the stack of layers has a peripheral portion made from a flowable mixture identical to the flowable mixture of the first and second external layers.