Solid electrolyte sheet and preparation method thereof, battery and device including the same
The present application provides a preparation method for a solid electrolyte, including: acquiring an initial reaction mixture including a lithium precursor, a central atom ligand and an organic solvent; acquiring a modified solution including a borate ester and the organic solvent; mixing the initial reaction mixture and the modified solution, and drying to acquire an initial product; performing a grinding, cold press and heat treatment to the initial product to obtain the solid electrolyte. In the preparation method provided by the present application, a B and O co-doped sulphide solid electrolyte can be obtained by modifying the sulphide solid electrolyte with the borate ester as a doping raw material. The ionic conductivity of the prepared sulphide solid electrolyte is significantly improved, which is also conducive to improvement of energy density of the all-solid-state batteries.
1. A preparation method for a solid electrolyte, comprising:
acquiring an initial reaction mixture comprising a lithium precursor, a central atom ligand and an organic solvent;
acquiring a modified solution comprising a borate ester and the organic solvent;
mixing the initial reaction mixture and the modified solution, and drying to obtain an initial product; and
performing a post-treatment to the initial product to obtain the solid electrolyte.
2. The preparation method for a solid electrolyte according to claim 1 , wherein the lithium precursor comprises one or more of Li 2 S and LiX, wherein X comprises one or more of F, Cl, Br and I.
3. The preparation method for a solid electrolyte according to claim 1 , wherein the central atom ligand comprises one or more of P 2 S 5 , SiS 2 , GeS 2 , B 2 S 3 and Al 2 S 3 .
4. The preparation method for a solid electrolyte according to claim 1 , wherein the borate ester has a structure shown in formula (I):
wherein R is selected from C1˜C4 alkyl.
5. The preparation method for a solid electrolyte according to claim 4 , wherein the borate ester is selected from one or more of structures (I-1) to (I-4):
6. The preparation method for a solid electrolyte according to claim 1 , wherein an amount of substance of the lithium precursor accounts for 70˜94% of a total amount of substance of the lithium precursor, central atom ligand and borate ester.
7. The preparation method for a solid electrolyte according to claim 1 , wherein an amount of substance of the central atom ligand accounts for 5˜25% of the total amount of substance of the lithium precursor, central atom ligand and borate ester.
8. The preparation method for a solid electrolyte according to claim 1 , wherein an amount of substance of the borate ester accounts for 0.1˜5% of the total amount of substance of the lithium precursor, central atom ligand and borate ester.
9. The preparation method for a solid electrolyte according to claim 1 , wherein, after mixing the initial reaction mixture and the modified solution, a sufficient dispersing is performed, and a time for the sufficient dispersing is 5˜20 hours.
10. The preparation method for a solid electrolyte according to claim 1 , wherein the cold press is a cold press molding under a cold press pressure of 50 to 200 MPa.
11. The preparation method for a solid electrolyte according to claim 1 , wherein a temperature range of the heat treatment is 400˜700° C.
12. The preparation method for a solid electrolyte according to claim 1 , wherein a time for the heat treatment is 0.5 to 5 hours.
13. A solid electrolyte obtained by the preparation method for a solid electrolyte according to claim 1 .
14. The solid electrolyte according to claim 13 , wherein a conductivity of the solid electrolyte is above 1.4 mS/cm.
15. The solid electrolyte according to claim 13 , wherein a battery capacity of the solid electrolyte is above 140 mAh/g.
16. A solid electrolyte sheet, the solid electrolyte sheet is prepared by the solid electrolyte prepared by the preparation method according to claim 1 .
17. An all-solid-state lithium ion battery, wherein the all-solid-state lithium ion battery is prepared by the solid electrolyte prepared by the preparation method according to claim 1 .
18. A stacked all-solid-state lithium ion battery, comprising:
a positive electrode sheet, a solid electrolyte sheet and a negative electrode sheet; wherein, the solid electrolyte sheet is the solid electrolyte sheet according to claim 16 .
19. A device, comprising:
the all-solid-state lithium ion battery according to claim 17 .