Formaldehyde-free highly water and abrasion resistant overlay for building products
A paper based overlay is provided. The overlay has a paper impregnated with a resin composition having an acrylic resin having a glass transition temperature in a range of from about −20° C. to about 40° C. and a resin content from about 15 to about 35 wt. % based on the weight of the overlay. The acrylic composition may include wax in the amount of about 0.005 to about 3.5 wt. % based on the weight of the resin composition. A method of producing the overlay is also provided. The overlay is highly water and abrasion resistant with low volatile content.
1. An overlay comprising paper impregnated with a resin composition, wherein said resin composition comprises:
a thermoplastic acrylic resin having a glass transition temperature in a range of from about −20 ° C. to about 40 ° C.,
wherein the acrylic resin content in the overlay is in a range of from about 15 wt. % to about 35 wt. % based on the weight of the overlay,
wherein the overlay is affixed to a substrate selected from the group consisting of a gypsum board, a wall board, and a panel, and
wherein the overlay is free of formaldehyde.
2. The overlay of claim 1 , wherein the glass transition temperature is in a range of from about 10° C. to about 35° C.
3. The overlay of claim 1 , wherein the overlay further comprises 0.0001 wt. % to about 3.5 wt. % a wax, based on a solid wax weight, and the wax has a melt point in a range of from about 15º C to about 85° C.
4. The overlay of claim 1 , wherein the overlay further comprises 0.0001 wt. % to about 3.5 wt. % a wax, based on a solid wax weight, and the wax is selected from slack wax, paraffin wax, Montan wax, microcrystalline wax, and mixture thereof.
5. The overlay of claim 1 , wherein the acrylic resin content in the overlay is in a range of from about 15.0 wt. % to about 32.5 wt. %, based on the weight of the overlay.
6. The overlay of claim 1 , wherein the resin composition further comprises a component selected from diols, release agents, antifoaming agents and wetting agents.
7. The overlay of claim 1 , wherein the paper is kraft paper.
8. The overlay of claim 7 , wherein the kraft paper has a basis weight in a range of from about 70 to about 90 g/m 2 .
9. The overlay of claim 7 , wherein the kraft paper has an ash content in a range of from about 5 to about 12 wt. % of the kraft paper.
10. The overlay of claim 1 , wherein the overlay further comprising an acrylic paint coating that comprises an acrylic resin.
11. The overlay of claim 10 , wherein the acrylic paint coating has a weight in a range of from about 25 to about 45 g/m 2 .
12. The overlay of claim 1 , wherein the overlay has a volatile content in a range of up to about 4%, based on the weight of the overlay.
13. The overlay of claim 1 , wherein the overlay has a water ingress less than 200 g/m 2 as measured using ASTM D-5795 and more than 500 cycles as measured using a Taber abraser in conjunction with a Calibrase CS-17 wheel.
14. A building product comprising an the overlay,
wherein the overlay comprising paper impregnated with a resin composition, wherein said resin composition comprises:
a thermoplastic acrylic resin having a glass transition temperature in a range of from about -20 ° C.to about 40 ° C.,
wherein the acrylic resin content in the overlay is in a range of from about 15 wt. % to about 35 wt. % based on the weight of the overlay,
wherein the overlay is affixed to a substrate selected from the group consisting of a gypsum board, a wall board, and a panel, and
wherein the overlay is free of formaldehyde.
15. The building product according to claim 14 , wherein the building product is a ceiling tile comprising gypsum board.
16. The building product according to claim 14 , wherein the building product has a Sound Transmission Class (STC) rating of about 30 to about 65 when tested in accordance with ASTM E90-04 and E413-04.