Catalyst system for curing phenolic resole resins
The present invention relates to a catalyst system which improves the work life of acid-catalyzed resole resins at higher ambient temperatures and provides extended shelf life. The catalyst system comprises an inorganic acid catalyst and one or more polyhydric alcohols. In particular, the present invention relates to a catalyst system wherein the inorganic acid and the alcohol do not convert to an ester when added to the resole resin.
1. A method for curing a resole resin comprising the steps of:
preparing a catalyst by mixing an inorganic acid, one or more polyhydric alcohols, and 1-4 wt % free morpholine, based on the total weight of the catalyst, that when reacted at a higher ambient temperature do not form an ester, and
mixing a resole resin with the catalyst, wherein the inorganic acid comprises phosphoric acid and the one or more polyhydric alcohols comprise glycerol and/or glycol and wherein the catalyst is prepared by mixing the phosphoric acid in a range of 20 to 70 wt %, the glycol and/or glycerol up to 50 wt %, and water in a range of 0 to 35 wt %.
2. The method as claimed in claim 1 , wherein the weight percentage of phosphoric acid: glycol and/or glycerol: water is in a ratio of 50:20:30.
3. An ester-free catalyst system for improving the cure time of acid-catalyzed resole resins at higher ambient temperatures, the catalyst system comprising:
20 to 70 wt %, phosphoric acid;
up to 50 wt %, glycol, glycerol or both;
up to 35 wt % solvent, and
1-4 wt % morpholine, based on a total weight of the catalyst system,
wherein the catalyst system does not form an ester when reacted at ambient temperatures of 35-45° C.
4. The catalyst system as claimed in claim 3 , wherein the higher ambient temperature includes 40° C.-45° C.
5. The method as claimed in claim 1 , wherein the higher ambient temperature includes 35-40° C.
6. The method as claimed in claim 1 , wherein the higher ambient temperature includes 40° C.-45° C.
7. The catalyst system as claimed in claim 3 , wherein the higher ambient temperature includes 35-40° C.
8. The ester-free catalyst system of claim 3 , wherein the solvent is water.
9. The ester-free catalyst system of claim 3 , wherein a weight ratio of the phosphoric acid to the glycol and/or glycerol is from 1:1 to 1:10.
10. The method as claimed in claim 1 , wherein a weight percentage of the catalyst is 2% to 20% of the resole.
11. The method as claimed in claim 1 , wherein a weight ratio of the inorganic acid to the one or more polyhydric alcohols is from 1:1 to 1:10.
12. The catalyst system as claimed in claim 3 , wherein the solvent is water or an aliphatic alcohol.
13. The catalyst system as claimed in claim 3 , wherein the weight percentage of phosphoric acid: glycol and/or glycerol: water solvent is in a ratio of 50:20:30.
14. A resole resin comprising the catalyst system as claimed in claim 3 .