Method for manufacturing a carpet or a rug and a carpet or rug obtained thereby
Method for manufacturing a carpet or a rug, comprising the following steps: the step (S 1 -S 2 ) of providing a primary backing ( 1 ), being a woven or non-woven layer comprising filaments ( 2 ) of polyethyleneterephthalate and copolymer of polyethyleneterephthalate, the coPET having a lower melting temperature than the PET and wherein said PET is available in said primary backing ( 1 ) in a higher amount than said coPET; the step of providing a glue layer ( 11 ) consisting for 50% or more out of coPET; the step of tufting yarn at least into said primary backing ( 1 ); the step of activating said glue layer ( 11 ) at least for partially fixing said yarn ( 12 ) on said primary backing ( 1 ). The invention also concerns carpets ( 16 ) and rugs that are obtained or obtainable by means of such method.
1. Method for manufacturing a carpet or a rug, wherein the method comprises at least the following steps:
the step of providing a primary backing;
the step of tufting yarn at least into said primary backing;
the step of activating a glue layer at least for partially fixing said yarn on said primary backing;
characterized in that
said primary backing comprises a sandwich consisting of, from top to bottom, a first primary backing, the glue layer, and a second primary backing; wherein
said glue layer is a layer comprising continuous bicomponent filaments having a core comprising polyethylene terephthalate (PET) and a sheath comprising a copolymer of polyethylene terephthalate (coPET), wherein the glue layer has a ratio of PET/coPET of about 20/80 by weight;
said first and second primary backings are layers of continuous bicomponent filaments having a core comprising PET and a sheath comprising coPET, wherein the PET is present in an amount of more than 50 percent; and
said first primary backing has a weight of 100 grams per square meter or higher, and said second primary backing has a weight of between 40 and 85 grams per square meter.
2. Method according to claim 1 , characterized in that said glue layer is a woven or nonwoven layer.
3. Method according to claim 1 , characterized in that said step of activating said glue layer is at least executed with heat and/or pressure.
4. Method according to claim 1 , characterized in that said yarn is a yarn based on PET.
5. Method according to claim 1 , wherein the method further comprises the step of adding a secondary backing layer.
6. Method according to claim 5 , characterized in that said secondary backing layer comprises an unsolid layer comprising a material selected from the group consisting of PET, coPET, or a combination thereof.
7. Method according to claim 6 , characterized in that said unsolid layer has internal cavities.
8. A carpet or rug comprising
a primary backing comprising a sandwich consisting of, from top to bottom, a first primary backing, an activated glue layer, and a second primary backing; wherein said glue layer is a layer comprising continuous bicomponent filaments having a core comprising polyethylene terephthalate (PET) and a sheath comprising copolymer of polyethylene terephthalate (coPET) wherein the glue layer has a ratio of PET/coPET of about 20/80 by weight; said first and second primary backings are layers of continuous bicomponent filaments having a core comprising PET and a sheath comprising coPET having the PET present in an amount of more than 50 percent; and said first primary backing has a weight of 100 grams per square meter or higher, and said second primary backing has a weight of between 40 and 85 grams per square meter; and
a tufted pile tufted on said primary backing, said pile being present at the top of the primary backing.
9. The carpet or rug according to claim 8 , wherein the carpet or rug further comprises a secondary backing layer.
10. The carpet or rug according to claim 9 , wherein said secondary backing layer comprises an unsolid layer comprising a material selected from the group consisting of PET, coPET, or a combination thereof.
11. The carpet or rug according to claim 10 , wherein said unsolid layer has internal cavities.