Crack sealant method and composition for reduced color contrast
A pigmented asphaltic sealant composition and methods of preparing and using the sealant composition which eliminate or reduce a color contrast between the sealant composition and the road, pavement, or other substrate surface to which the sealant composition is applied.
1. An asphaltic sealant composition comprising:
asphalt in an amount in a range of from 50% to 89% by weight based upon a total weight of the asphaltic sealant composition, the asphalt having a jet black color;
a pigment dispersed in the asphalt in an amount in a range of from 10% to 30% by weight based upon the total weight of the asphaltic sealant composition, and at a degree of dispersion, which changes the jet black color of the asphalt to a color ranging from dark brown to light brown or tan; and
an epoxidized ester of a vegetable oil in an amount in a range of from 1% to 5% by weight based upon the total weight of the asphaltic sealant composition which increases dispersion and reduces sedimentation of the pigment in the asphalt.
2. The asphaltic sealant composition of claim 1 comprising the epoxidized ester of the vegetable oil being an epoxidized ester of soybean oil.
3. The asphaltic sealant composition of claim 1 comprising the pigment being rutile titanium dioxide.
4. The asphaltic sealant composition of claim 1 further comprising:
a radial SBS polymer and/or a linear SBS polymer in a total amount in a range of from 3% to 8% by weight based upon the total weight of the asphaltic sealant composition and/or
crumb rubber in an amount in a range of from 3% to 8% by weight based upon the total weight of the asphaltic sealant composition.
5. The asphaltic sealant composition of claim 4 comprising:
the epoxidized ester of the vegetable oil being an epoxidized ester of soybean oil;
the pigment being rutile titanium dioxide;
the pigment being present in an amount of from 15% to 25% by weight based upon the total weight of the asphaltic sealant composition;
the epoxidized ester of soybean oil being present in an amount of from 2% to 5% by weight based upon the total weight of the asphaltic sealant composition;
the radial SBS polymer and/or the linear SBS polymer being present in a total amount of from 3% to 8% by weight based upon the total weight of the asphaltic sealant composition; and
the crumb rubber being present in an amount of from 3% to 8% by weight based upon the total weight of the asphaltic sealant composition.
6. The asphaltic sealant composition of claim 5 comprising the epoxidized ester of soybean oil being an epoxy functionalized methyl ester of soybean oil.
7. An asphaltic sealant composition comprising:
asphalt in an amount in a range of from 50% to 89% by weight based upon a total weight of the asphaltic sealant composition, the asphalt having a jet black color;
a pigment dispersed in the asphalt in an amount in a range of from 10% to 30% by weight based upon the total weight of the asphaltic sealant composition, and at a degree of dispersion, which changes the jet black color of the asphalt to a red color; and
an epoxidized ester of a vegetable oil in an amount in a range of from 1% to 5% by weight based upon the total weight of the asphaltic sealant composition which increases dispersion and reduces sedimentation of the pigment in the asphalt.
8. The asphaltic sealant composition of claim 7 further comprising the epoxidized ester of the vegetable oil being an epoxidized ester of soybean oil.
9. The asphaltic sealant composition of claim 7 further comprising the pigment being iron (III) oxide.
10. The asphaltic sealant composition of claim 7 further comprising:
a radial SBS polymer and/or a linear SBS polymer in a total amount in a range of from 3% to 8% by weight based upon the total weight of the asphaltic sealant composition and/or
crumb rubber in an amount in a range of from 3% to 8% by weight based upon the total weight of the asphaltic sealant composition.
11. The asphaltic sealant composition of claim 10 further comprising:
the epoxidized ester of the vegetable oil being an epoxidized ester of soybean oil;
the pigment being iron (III) oxide;
the pigment being present in an amount of from 15% to 25% by weight based upon the total weight of the asphaltic sealant composition;
the epoxidized ester of soybean oil being present in an amount of from 2% to 5% by weight based upon the total weight of the asphaltic sealant composition;
the radial SBS polymer and/or the linear SBS polymer being present in a total amount of from 3% to 8% by weight based upon the total weight of the asphaltic sealant composition; and
the crumb rubber being present in an amount of from 3% to 8% by weight based upon the total weight of the asphaltic sealant composition.
12. The asphaltic sealant composition of claim 11 further comprising the epoxidized ester of soybean oil being an epoxy functionalized methyl ester of soybean oil.