Conductive high strength extrudable ultra high molecular weight polymer graphene oxide composite

1. An injection-moldable or extrudable composite comprising;

a powder or pellets of a polymer comprising ultra-high molecular weight polyethylene (UHMWPE) and one or more substances selected from cross-linked polyethylene (PEX), linear low-density polyethylene (LLDPE), low-density polyethylene (LDPE), medium-density polyethylene (MDPE), para-aramid fibers, or polyoxazole fibers; and

graphene/graphite oxide or graphene oxide;

wherein the composite enhances or preserves at least 80% of primary physical properties of a compression-molded version of the polymer.

2. The composite of claim 1 , wherein physical properties of a compression-molded UHMWPE comprise a resistivity less than 1011 ohm-cm.

3. The composite of claim 1 , wherein the UHMWPE has a molecular weight between 500,000 and 16,000,000 daltons or between 2,000,000 and 8,000,000 daltons.

4. The composite of claim 1 , wherein the composite has a graphene oxide loading of 0.1 wt %, 0.5 wt %, 1.0 wt %, 1.25 wt %, 1.5 wt %, 1.75 wt %, 2.0 wt %, 2.25 w %, 2.5 w %, 2.75 wt %, 3.0 wt %, 3.25 wt %, 3.5 wt %, 3.75 wt %, 4.0 wt %, 4.25 wt %, 4.5 wt %, 4.75 wt %, 5.0 wt %, 6.0 wt %, 7.0 wt %, 8.0 wt %, 9.0 wt %, 10 wt %, 11 wt %, 12 wt %, 13 wt %, 14 wt %, 15 wt %, 16 wt %, 17 wt %, 18 wt %, 19 wt %, or 20 wt % relative to the UHMWPE; or

the composite has a polypropylene loading of 0.1 wt %, 0.5 wt %, 1.0 wt %, 1.25 wt %, 1.5 wt %, 1.75 wt %, 2.0 wt %, 2.25 w %, 2.5 w %, 2.75 wt %, 3.0 wt %, 3.25 wt %, 3.5 wt %, 3.75 wt %, 4.0 wt %, 4.25 wt %, 4.5 wt %, 4.75 wt %, 5.0 wt %, 6.0 wt %, 7.0 wt %, 8.0 wt %, 9.0 wt %, 10 wt %, 11 wt %, 12 wt %, 13 wt %, 14 wt %, 15 wt %, 16 wt %, 17 wt %, 18 wt %, 19 wt %, or 20 wt % relative to the UHMWPE.

5. The composite of claim 1 , wherein the graphene/graphite oxide comprises graphene/graphite oxide flakes with a surface area to thickness ratio greater than 300 angstroms, and a thickness of less than 160 angstroms, wherein the graphene flakes have no significant physical surface distortions, no significant epoxy functionalization, and an oxidation level greater than 0.5% by mass; or

wherein at least 95% of the graphene/graphite oxide comprises graphene/graphite oxide flakes with a thickness of about 0.8 to 20 nm.

6. The composite of claim 1 , wherein at least one of: a mechanical, an electrical, or a thermal physical property of the polymer is enhanced or sustained with addition of the graphene/graphite oxide or graphene oxide when compared to the polymer without the graphene/graphite oxide or graphene oxide.

7. The composite of claim 1 , wherein UHMWPE comprises a powder with a particle size between 15 μm and 1,000 μm; or the polypropylene comprises a powder with a particle size between 100 μm and 2,500 μm.

8. A method of making an extrudable and injection-moldable comprising:

mixing a powder or pellets of a polymer comprising ultra-high molecular weight polyethylene (UHMWPE) and one or more other substances with between 0.01 wt % and 20 wt % graphene and/or graphene oxide, wherein the one or more other substances comprise at least one of cross-linked polyethylene (PEX), linear low-density polyethylene (LLDPE), low-density polyethylene (LDPE), medium-density polyethylene (MDPE), para-aramid fibers, or polyoxazole fibers, and wherein the composite preserves or enhances at least one mechanical, electrical, or thermal physical property relative to a compression-molded composite of the polymer and the graphene oxide.

9. The method of claim 8 , wherein physical properties of a polymer comprises a resistivity less than 1011 ohm-cm.

10. The method of claim 8 , wherein the UHMWPE has a molecular weight between 500,000 and 16,000,000 daltons or between 2,000,000 and 8,000,000 daltons.

11. The method of claim 8 , wherein the composite has a graphene oxide loading of 0.1 wt %, 0.5 wt %, 1.0 wt %, 1.25 wt %, 1.5 wt %, 1.75 wt %, 2.0 wt %, 2.25 w %, 2.5 w %, 2.75 wt %, 3.0 wt %, 3.25 wt %, 3.5 wt %, 3.75 wt %, 4.0 wt %, 4.25 wt %, 4.5 wt %, 4.75 wt %, 5.0 wt %, 6.0 wt %, 7.0 wt %, 8.0 wt %, 9.0 wt %, 10 wt %, 11 wt %, 12 wt %, 13 wt %, 14 wt %, 15 wt %, 16 wt %, 17 wt %, 18 wt %, 19 wt %, or 20 wt % relative to the UHMWPE; or

the composite has a polypropylene loading of 0.1 wt %, 0.5 wt %, 1.0 wt %, 1.25 wt %, 1.5 wt %, 1.75 wt %, 2.0 wt %, 2.25 w %, 2.5 w %, 2.75 wt %, 3.0 wt %, 3.25 wt %, 3.5 wt %, 3.75 wt %, 4.0 wt %, 4.25 wt %, 4.5 wt %, 4.75 wt %, 5.0 wt %, 6.0 wt %, 7.0 wt %, 8.0 wt %, 9.0 wt %, 10 wt %, 11 wt %, 12 wt %, 13 wt %, 14 wt %, 15 wt %, 16 wt %, 17 wt %, 18 wt %, 19 wt %, or 20 wt % relative to the UHMWPE.

12. The method of claim 8 , wherein the graphene/graphite oxide are graphene/graphite oxide flakes with a surface area to thickness ratio greater than 300 angstroms, and thickness of less than 160 angstroms, wherein the graphene/graphite oxide flakes have no significant physical surface distortions, no significant epoxy functionalization, and have an oxidation level greater than 0.5% by mass; or wherein at least 95% of the graphene/graphite oxide comprises graphene/graphite oxide flakes with a thickness of about 0.8 to 20 nm.

13. The method of claim 8 , or the UHMWPE comprises a powder with a particle size between 15 μm and 1,000 μm, or the polypropylene comprises a powder with a particle size between 100 μm and 2,500 μm.

14. The method of claim 8 , further comprising at least one of:

heating a composite of UHMWPE, graphene oxide, and polypropylene during the mixing step;

coating a UHMWPE powder with graphene or graphite oxide by combining the UHMWPE powder and the graphene or graphite oxide powder in a high shear mixer for more than 1 minute and less than 60 minutes;

adding a polypropylene powder to a graphene or graphite oxide coated UHMWPE powder and combining in a high shear mixer for more than 1 minute and less than 60 minutes;

placing a mix of UHMWPE, graphene oxide, and polypropylene powder into an extruder to produce pellets for use in injection molding;

obtaining graphene/graphite oxide flakes formed in a stirred media mill, wherein the stirred media mill is an Attrition mill or ball mill; or

extruding the composite in a cylinder at a temperature between 200° C. and 250° C.; with a melt temperature between 180° C. and 400° C. or between 200° C. and 240° C.; and a screw speed between 60 to 300 rpm.

15. The method of claim 8 , wherein at least one of a mechanical, electrical, or thermal physical property of the composite is enhanced with the addition of the graphene/graphite oxide.

16. The method of claim 8 , wherein the graphene/graphite oxide comprises graphene/graphite oxide flakes and at least 95% of the graphene/graphite oxide flakes have a surface area to thickness ratio of a minimum of 300 angstroms; or wherein the graphene/graphite oxide flake has primarily edge oxidation.

17. The method of claim 8 further comprising:

extruding or injection molding the composite into a shape.

18. An injection-moldable or extrudable composite comprising:

an Ultra High Molecular Weight Polyethylene (UHMWPE) and one or more substances selected from cross-linked polyethylene (PEX), linear low-density polyethylene (LLDPE), low-density polyethylene (LDPE), medium-density polyethylene (MDPE), para-aramid fibers, and/or polyoxazole fibers; and

graphene/graphite oxide or graphene oxide;

wherein the composite enhances or preserves at least 80% of primary physical properties of a compression-molded version of the polymer.