Laminating adhesives using polyester from transesterification of polylactic acid with natural oils
A specific mixture of polyols, at least one of which contains the transesterification product of the polymer polylactic acid with natural oils. The mixture of polyols can be used as one component of a two-component adhesive for laminating flexible packaging. The other component comprises an isocyanate-functionalized compound. The two components are combined before use and the resulting adhesive can be used to bond films to form a flexible packaging material.
1. An isocyanate reactive component for reaction with an isocyanate functionalized component to form a two-component laminating adhesive, comprising:
a transesterification product of a reaction mixture comprising polymeric polylactic acid and at least one natural oil; and
a high OH functionality polyol product
and wherein the reaction mixture comprises: polylactic acid present in an amount of from 50 to 85 weight percent based on a total weight of the reaction mixture; at least one natural oil present in an amount of from 13 to 30 weight percent based on the total weight of the reaction mixture; a diol present in an amount of from 2 to 36 weight percent based on the total weight of the reaction mixture; and optionally, a transesterification catalyst.
2. The isocyanate reactive component of claim 1 wherein the reaction mixture comprises polymeric polylactic acid, at least one natural oil and a diol having a molecular weight of about 50 to about 2000 daltons.
3. The isocyanate reactive component of claim 1 having a renewable content in the range of at least 70%.
4. The isocyanate reactive component of claim 1 having a viscosity of 3,000 to 20,000 cps at 25° C.
5. The isocyanate reactive component of any of claim 1 wherein the high OH functionality polyol product has at least about two primary hydroxyl groups and at least about two secondary hydroxyl groups.
6. The isocyanate reactive component of claim 1 wherein the natural oil is castor oil and/or soybean oil.
7. A two-component adhesive for laminating flexible packaging material including a Component A and a Component B, wherein:
Component A comprises an isocyanate functionalized compound having two or more terminal isocyanate groups per molecule; and
Component B comprises the isocyanate reactive component including a transesterification product of a reaction mixture comprising polymeric polylactic acid and at least one natural oil; and a high OH functionality polyol product.
8. The two-component adhesive of claim 7 wherein the isocyanate functionalized compound is prepared using one or more polyisocyanates.
9. The two-component adhesive of claim 7 wherein the isocyanate functionalized compound is prepared using diphenylmethane diisocyanate, a modified version of diphenylmethane diisocyanate and combinations thereof.
10. The two-component adhesive of claim 7 wherein the isocyanate functionalized compound comprises a polyurethane prepolymer reaction product of at least one polyol and an excess of a polyisocyanate.
11. Cured reaction products of the two-component adhesive claim 7 .
12. Cured reaction products of the two-component adhesive of claim 7 having a minimum room temperature bond strength of 200 grams/inch.
13. Cured reaction products of the two-component adhesive of claim 7 having a minimum room temperature bond strength of 400 grams/inch.
14. A flexible laminate comprising the two-component adhesive of claim 7 disposed between a first film surface and a second film surface.
15. A flexible laminate comprising cured reaction products of the two-component adhesive of claim 7 disposed between a first film surface and a second film surface.
16. A food container comprising a food product disposed between layers of flexible laminate, the flexible laminate comprising cured reaction products of the two-component adhesive of claim 7 bonding adjacent films.