Antibacterial biomedical implants and associated materials, apparatus, and methods
Methods for improving the antibacterial characteristics of biomedical implants and related implants manufactured according to such methods. In some implementations, a biomedical implant comprising a silicon nitride ceramic material may be subjected to a surface roughening treatment so as to increase a surface roughness of at least a portion of the biomedical implant to a roughness profile having an arithmetic average of at least about 500 nm Ra. In some implementations, a coating may be applied to a biomedical implant. Such a coating may comprise a silicon nitride ceramic material, and may be applied instead of, or in addition to, the surface roughening treatment process.
1. A method for improving the antibacterial characteristics of a biomedical implant, the method comprising the steps of:
providing a biomedical implant comprising a poly-ether-ether-ketone (PEEK) and/or titanium substrate material; and
applying a coating of SiYAION on the biomedical implant by chemical vapor deposition (CVD), physical vapor deposition (PVD), plasma spraying, electro-deposition, electrophoretic deposition, slurry coating, or high-temperature diffusion, wherein the SiYAION coating has a thickness of 1 μm to 125 μm.
2. The method of claim 1 , wherein the SiYAION is β-SiYAION.
3. The method of claim 1 , wherein the coated biomedical implant has increased bacterial resistance as compared to the substrate material alone.
4. The method of claim 1 , wherein the biomedical implant comprises an intervertebral spinal implant.
5. The method of claim 1 , wherein the biomedical implant comprises PEEK.
6. The method of claim 1 , wherein the biomedical implant comprises titanium.
7. A biomedical implant with improved antibacterial characteristics comprising:
a poly-ether-ether-ketone (PEEK) and/or titanium substrate material; and
a coating on the substrate material comprising β-SiYAION, wherein the coating has a thickness of 1 μm to 125 μm,
wherein the coating is applied to the substrate material by chemical vapor deposition (CVD), physical vapor deposition (PVD), plasma spraying, electro-deposition, electrophoretic deposition, slurry coating, or high-temperature diffusion.
8. The biomedical implant of claim 7 , wherein the biomedical implant has increased bacterial resistance as compared to the substrate material alone.
9. The biomedical implant of claim 7 , wherein the substrate material comprises PEEK.
10. The biomedical implant of claim 7 , wherein the substrate material comprises titanium.
11. The biomedical implant of claim 7 , wherein the biomedical implant is selected from an intervertebral spinal implant, a hip implant, an orthopedic plate, or a bone screw.
12. The biomedical implant of claim 7 , wherein the biomedical implant comprises a titanium bone screw.
13. A biomedical implant with improved antibacterial characteristics comprising:
a polymeric substrate material filled with about 10 vol. % to about 20 vol. % of a powder comprising β-SiYAION
wherein the biomedical implant is selected from an intervertebral spinal implant, a hip implant, an orthopedic plate, or a bone screw.
14. The biomedical implant of claim 13 , wherein the substrate material comprises poly-ether-ether-ketone (PEEK).