Preparation method of solid catalyst for propylene polymerization
Disclosed is a method for preparing a solid catalyst for propylene polymerization, and more specifically, a method for preparing a solid catalyst for propylene polymerization including (1) first reacting dialkoxy magnesium and titanium halide compound under the presence of an organic solvent; (2) adding two kinds of non-aromatic internal electron donors to a product of the step (1) and reacting the mixture; and (3) second reacting the product of the step (2) with a titanium halide compound and washing a reaction product. The catalyst prepared according to the method as described in the present disclosure not only may provide high catalytic activity, but also may provide a propylene polymer having excellent stereoregularity.
1. A method for preparing a solid catalyst for propylene polymerization, the method comprising:
(1) reacting dialkoxy magnesium and titanium halide compounds under presence of an organic solvent;
(2) reacting a product of the step (1) with an internal electron donor mixture, wherein the internal electron donor mixture includes a mixture between 1,4-cyclohexadiene-1,2-dicarboxylic acid 1,2-dibutylester (A) and 9,9-bis(methoxymethyl)fluorene (C) or 2-isopropyl-2-isopentyl-1,3-dimethoxypropane (D):
(3) reacting the product of the step (2) with a titanium halide compound, and washing the product thereof.
2. The method of claim 1 , wherein the dialkoxy magnesium compound is diethoxy magnesium.
3. The method of claim 1 , wherein the titanium halide is represented by a general formula (I):
Ti(OR) a X (4-a) (I)
where R represents an alkyl group of 1 to 10 carbon atoms, X represents a halogen element, and a is an integer of 0 to 3 to satisfy a valence of the general formula.