Atomized anti-scratching nano-coating for glass surface and method of manufacturing thereof
A durable, hydrophobic and anti-scratching nano-coating for coating on a glass substrate or surface having a water contact angle of about 90° or more, a reduced coefficient of friction by 50% or more, and a reduced surface roughness compared to those of the glass substrate or surface without the nano-coating is provided, which includes a layer of fluorinated silica derived from sol-gel hydrolysis between one or more tetraalkoxysilanes having at least three alkoxy groups and one or more polyfluorinated silanes having at least a trialkoxysilane and from 15 to 17 fluorine atoms in the presence of a catalyst to a reaction mixture of the sol-gel hydrolysis between the one or more tetraalkoxysilanes and the one or more polyfluorinated silanes, and a solvent. A related method of fabricating the nano-coating via atomization of acid-containing or alkali-containing solution and sol-gel precursor solution onto the glass surface is also provided.
1. A durable, hydrophobic and anti-scratching nano-coating on a glass substrate or surface having a water contact angle of about 90° or more, a reduced coefficient of friction by 50% or more compared to the coefficient of friction of the glass substrate or surface without said nano-coating, and a reduced surface roughness of at least four times compared to the glass substrate or surface without said nano-coating, comprising:
a pretreated glass substrate or surface, the glass substrate or surface having been pretreated by an acid-containing solution comprising at least one stronger acid and one weaker acid and hydrogen peroxide;
a layer of fluorinated silica derived from sol-gel hydrolysis between one or more tetraalkoxysilanes and one or more polyfluorinated silanes having at least a trialkoxysilane and from 15 to 17 fluorine atoms in the presence of a catalyst to a reaction mixture of the sol-gel hydrolysis between the one or more tetraalkoxysilanes and the one or more polyfluorinated silanes, and a solvent.
2. The nano-coating of claim 1 , wherein the one or more tetraalkoxysilanes is/are represented by the following formula:
wherein OR′ is selected from an aliphatic or cycloaliphatic alkoxy group.
3. The nano-coating of claim 1 , wherein the one or more tetraalkoxysilanes is/are represented by the following formulae (I) and (II):
4. The nano-coating of claim 1 , wherein the one or more polyfluorinated silanes is/are represented by the following formula:
wherein OR′ is selected from an aliphatic or cycloaliphatic alkoxy group.
5. The nano-coating of claim 1 , wherein the one or more polyfluorinated silanes is/are represented by the following formulae (III) and (IV):
6. The nano-coating of claim 1 , wherein the one or more tetraalkoxysilanes and one or more polyfluorinated silanes are in weight ratio from 1:3 to 3:1.
7. The nano-coating of claim 1 , wherein the stronger acid is selected from hydrochloric acid and the weaker acid is selected from phosphoric acid and the weight ratio of the stronger and weaker acids is from 2:1 to 1:2.
8. The nano-coating of claim 1 , wherein the sol-gel hydrolysis is performed under compressed air and at a temperature from 15 to 30° C.
9. The nano-coating of claim 1 , wherein the catalyst is less than 5 wt % of the sol-gel hydrolysis reaction mixture.
10. The nano-coating of claim 9 , wherein the catalyst is ammonia solution.
11. The nano-coating of claim 1 , wherein the solvent is methanol.
12. The nano-coating of claim 1 , wherein the nano-coating has a thickness of about 100 nm or lower.
13. The nano-coating of claim 1 , wherein the nano-coating is substantially transparent to visible light.
14. A method of fabricating the durable, hydrophobic and anti-scratching nano-coating on a glass or substrate or surface of claim 1 , comprising:
pretreating a glass substrate or surface with an acid-containing solution comprising at least one stronger acid and one weaker acid and hydrogen peroxide;
synthesizing a sol-gel precursor solution comprising one or more tetraalkoxysilanes, one or more polyfluorinated silanes having at least a trialkoxysilane and from 15 to 17 fluorine atoms, and a solvent, and the one or more tetraalkoxysilanes and the one or more polyfluorinated silanes being hydrolyzed in the presence of a catalyst and the solvent;
atomizing the acid-containing solution into an atomization chamber such that surface roughness and water contact angle of the glass surface or substrate are reduced;
atomizing the sol-gel precursor solution into the atomization chamber to form the nano-coating onto the glass substrate such that water contact angle of the glass surface or substrate is increased to at least about 90° and coefficient of friction of the glass surface or substrate is reduced by at least 50%;
obtaining the glass substrate coated with the nano-coating after evacuating the atomization chamber.
15. The method of claim 14 , wherein said atomizing is performed at a temperature from 15 to 30° C.
16. The method of claim 14 , wherein the one or more tetraalkoxysilanes and one or more polyfluorinated silanes are in weight ratio from 1:3 to 3:1.
17. The method of claim 14 , wherein, said at least one stronger acid is selected from hydrochloric acid and said at least one weaker acid is selected from phosphoric acid, and the stronger and weaker acids have a weight ratio of 2:1 to 1:2.
18. The method of claim 14 , wherein the one or more tetraalkoxysilanes is/are represented by the following formulae (I) and (II):
19. The method of claim 14 , wherein the one or more polyfluorinated silanes is/are represented by the following formula:
wherein OR′ is selected from an aliphatic or cycloaliphatic alkoxy group.
20. The method of claim 14 , wherein the one or more polyfluorinated silanes is/are represented by the following formulae (III) and (IV):
21. The method of claim 14 , wherein the catalyst is ammonia solution.
22. The method of claim 14 , wherein the solvent is methanol.