Ultra-high flow styrene acrylonitrile copolymer compositions
Thermoplastic molding composition comprising (A) 40 to 80 wt.-% SAN copolymer (S/AN-ratio 78:22 to 65:35, Mw 80,000 to 250,000 g/mol); (B) 20 to 60 wt.-% SBC block copolymer (monovinylarene 61 to 64 wt.-%) comprising conjugated diene/monovinylarene tapered polymer blocks; and (C) 0 to 5 wt.-% additives and/or processing aids (C); exhibiting ultra-high melt flow with good mechanical, thermal and optical properties, a process for its preparation and its use for the production of bulky and/or thin walled articles.
1. A thermoplastic molding composition comprising components A, B, and C:
(A) 40 to 80 wt.-% of at least one copolymer (A) of styrene and acrylonitrile in a weight ratio of from 78:22 to 65:35, wherein the styrene and/or acrylonitrile is optionally partially replaced by methyl methacrylate, maleic anhydride, N-phenylmaleimide, and/or 4-phenylstyrene; wherein copolymer (A) has a weight average molar mass M w of 80,000 to 150,000 g/mol;
(B) 20 to 60 wt.-% of at least one coupled conjugated diene/monovinylarene block copolymer (B) comprising at least three consecutive conjugated diene/monovinylarene tapered polymer blocks, wherein in the final block copolymer all conjugated diene is incorporated into the tapered polymer block, and, based on the total weight of the final block copolymer, the monovinylarene is present in an amount of 61 to 64 wt.-%, and the conjugated diene is present in an amount of 36 to 39 wt.-%; and
(C) 0 to 5 wt.-% additives and/or processing aids (C);
wherein the components A, B, and, if present, C, sum to 100 wt.-%.
2. The thermoplastic molding composition according to claim 1 , comprising:
55 to 70 wt.-% component (A),
30 to 45 wt.-% component (B), and
0 to 5 wt.-% component (C).
3. The thermoplastic molding composition according to claim 1 , wherein copolymer (A) is a copolymer of styrene and acrylonitrile in a weight ratio of from 75:25 to 70:30.
4. The thermoplastic molding composition according to claim 1 , wherein M w of copolymer (A) is 90,000 to 150,000 g/mol.
5. The thermoplastic molding composition according to claim 1 , wherein in block copolymer (B) the conjugated diene is 1,3-butadiene and the monovinylarene is styrene.
6. The thermoplastic molding composition according to claim 1 , wherein in each individual tapered polymer block of block copolymer (B) the monovinylarene is present in an amount of from 2 to 18 wt.-%, based on the total weight of the final block copolymer, and the conjugated diene is present in an amount of from 8 to 17 wt.-%, based on the total weight of the final block copolymer.
7. The thermoplastic molding composition according to claim 1 , where the block copolymer (B) comprises at least one polymer chain S1-S2-B1/S3-B2/S4-B3/S5˜, wherein S1 and S2 are monovinylarene blocks, blocks B1/S3, B2/S4, B3/S5 are tapered blocks containing a mixture of monovinylarene and conjugated diene, and ˜ is the bond to the coupling agent.
8. The thermoplastic molding composition according to claim 1 , wherein in each tapered polymer block of block copolymer (B) the conjugated diene is present in an amount of from 0.6 parts to 4 parts per part monovinylarene in the tapered polymer block.
9. A process for the preparation of the thermoplastic molding composition according to claim 1 by melt mixing the components (A), (B), and, if present, (C), at temperatures in the range of from 180° C. to 250° C.
10. A method of using the thermoplastic molding composition according to claim 1 to produce a shaped article.
11. A shaped article made from the thermoplastic molding composition according to claim 1 .
12. A washing machine lid made from the thermoplastic molding composition according to claim 1 .
13. A pen made from the thermoplastic molding composition according to claim 1 .