Method for recycling thermoplastic by short depolymerisation

1. A process for the recycling of an article comprising

a thermoplastic polymer P 1 resin, wherein the article based on said thermoplastic polymer P 1 is an article made of composite material which additionally comprises a reinforcement,

said thermoplastic polymer P 1 having been formed from base monomers, said process comprising the following stages:

heating said resin by locally heating several zones of the resin in order to convert, at least in part, the thermoplastic polymer P 1 into at least two polymers P 2 , said at least two polymers P 2 having a lower molar mass than the molar mass of said polymer P 1 , wherein the locally heating several zones of the resin is carried out by means of pulsed electric fields at a temperature between 300° C. and 450° C.;

cooling said at least two polymers P 2 obtained after heating to a temperature substantially equal to or lower than the boiling point of said base monomers,

dissolving said at least two polymers P 2 in a solution comprising said base monomers; and

filtering solids from said reinforcement after dissolution of the polymers P 2 in the base monomers.

2. The recycling process as claimed in claim 1 , wherein the thermoplastic polymer P 1 resin is a resin of poly (methyl methacrylate), of polystyrene or of a mixture of these polymers.

3. The recycling process as claimed in claim 1 , wherein the thermoplastic polymer P 1 resin is a poly (methyl methacrylate) resin.

4. The recycling process as claimed in claim 1 , wherein the thermoplastic polymer P 1 resin is a (meth) acrylic polymer.

5. The recycling process as claimed in claim 1 , wherein the thermoplastic polymer P 1 resin is a (meth) acrylic polymer comprising at least 70% by weight of methyl methacrylate.

6. The recycling process as claimed in claim 1 , wherein the heating stage is repeated until a loss in weight of the thermoplastic polymer P 1 resin of between 10% and 90%, with respect to the initial total weight of the polymer P 1 resin, is obtained.

7. The recycling process as claimed in claim 1 , wherein the pulsed electric fields correspond to a plurality of electric discharges.

8. The recycling process as claimed in claim 1 , wherein the heating stage consists in heating by pulses with a duration of between 1 and 1000 μs.

9. The recycling process as claimed in claim 1 , wherein said base monomers included in the solution used to dissolve said at least two polymers P 2 originate at least in part from the recycling of another article based on said thermoplastic polymer P 1 resin.

10. The recycling process as claimed in claim 1 , wherein the local heating temperature is between 350° C. and 450° C.

11. The recycling process as claimed in claim 1 , wherein the cooling stage is carried out down to a temperature of less than or equal to 250° C.

12. The recycling process as claimed in claim 1 , wherein the cooling stage is carried out down to a temperature of greater than 30° C.

13. The recycling process as claimed in claim 1 wherein the cooling stage comprises a heat recovery stage.

14. The recycling process as claimed in claim 1 , wherein the dissolution stage comprises a stage of bringing into contact at least one times the amount by weight of the base monomers with respect to the initial weight of the article to be recycled.

15. The recycling process as claimed in claim 1 , wherein the process comprises a stage of recovery of the base monomers in the gaseous state, formed during the heating stage.

16. The recycling process as claimed in claim 1 , wherein the process further comprises a preheating stage.

17. The recycling process as claimed in claim 16 , wherein the process comprises a stage of preheating up to a temperature of less than 200° C.